Abstract:The paper introduced the fabricating technology of tungsten plasma facing material (W-PFM), such as plasma spraying technology and powder metallurgy with dispersed Lanthanum oxide (La2O3). And it was studied that the micro-structure and the main performances of tungsten materials as PFM. The results indicate that VPS-W coating has the better properties compared to APS-W coating: the lower porosity, the better thermal conductivity, the lower impurity content and the better heat flux performance. It can withstand 100 fatigue cycles under the heat flux of 10MW/m2 and is more appropriate for plasma facing material. La2O3 particles can hold back W particle growing and enhance the strength of tungsten, which are helpful to improve thermal performance of W PFM. And W-1wt.%La2O3 as PFM is suitable under the heat flux of no more 6MW/m2.