-1范圍內的熱塑性行為。推導了該溫度和應變速率下的本構方程，得到了該溫度范圍內的熱加工圖。用電子背散射衍射研究了合金壓縮后的動態(tài)再結晶。確定了失穩(wěn)區(qū)的位置，并表明在熱變形條件下，確實發(fā)生了動態(tài)再結晶，獲得了細小的晶粒。Inconel 617熱處理的最佳溫度范圍為1075~1175 ℃，該溫度范圍處于材料的安全區(qū)。;To solve the problems of processing Inconel 617 alloy at high temperatures, the hot deformation behavior of forged Inconel 617 at high temperature was studied. A Gleeble-3500 instrument was used to analyze the thermoplastic behavior in the temperature range of 900~1200 °C and strain rate range of 0.001~10 s-1. The constitutive equation in this temperature and strain rate range was deduced, and the thermal processing map was obtained. The dynamic recrystallization after compression was studied by electron backscatter diffraction. The location of the instability zone was determined. Results show that under the conditions of thermal deformation, dynamic recrystallization occurs, and fine grains are obtained. The optimal temperature range for Inconel 617 thermal processing is identified as 1075~1175 °C, and this temperature range is in the stable zone for the material."/>