二氧化硅氣凝膠復(fù)合材料可重復(fù)使用性能研究
DOI:
作者:
作者單位:

西安理工大學(xué)材料科學(xué)與工程學(xué)院,國防科學(xué)技術(shù)大學(xué)新型陶瓷纖維及其復(fù)合材料重點實驗室,國防科學(xué)技術(shù)大學(xué)新型陶瓷纖維及其復(fù)合材料重點實驗室,西安理工大學(xué)材料科學(xué)與工程學(xué)院,國防科學(xué)技術(shù)大學(xué)新型陶瓷纖維及其復(fù)合材料重點實驗室

作者簡介:

通訊作者:

中圖分類號:

基金項目:

國家自然科學(xué)基金資助(項目號51702360)


The Research on Reusable Properties of Silica Aerogel Composites
Author:
Affiliation:

School of Materials Science and Engineering,Xi’an University of Technology,Xi’an,Science and Technology on Advanced Ceramic Fibers and Composites Laboratory,National University of Defense Technology,Science and Technology on Advanced Ceramic Fibers and Composites Laboratory,National University of Defense Technology,School of Materials Science and Engineering,Xi’an University of Technology,Xi’an,Science and Technology on Advanced Ceramic Fibers and Composites Laboratory,National University of Defense Technology

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    為研究二氧化硅氣凝膠復(fù)合材料可重復(fù)使用性能,根據(jù)二氧化硅氣凝膠復(fù)合材料的實際使用情況,對二氧化硅氣凝膠復(fù)合材料在400℃下單面加熱10次,每次保溫1800s,通過對其質(zhì)量損失率、尺寸收縮率、隔熱性能、微觀結(jié)構(gòu)變化進行監(jiān)測的手段對二氧化硅氣凝膠復(fù)合材料在400℃下的穩(wěn)定性進行評價。結(jié)果表明,經(jīng)過10次單面加熱的二氧化硅氣凝膠復(fù)合材料表現(xiàn)出了優(yōu)異的穩(wěn)定性能,其中質(zhì)量損失率、XYZ方向尺寸收縮率、常溫?zé)釋?dǎo)率、高溫?zé)釋?dǎo)率以及微觀結(jié)構(gòu)變化都非常小。綜合來看,二氧化硅氣凝膠復(fù)合材料在400℃下單面加熱10次的使用條件下能夠安全使用。

    Abstract:

    In order to research the reusability of the high speed flight vehicle in the future, according to the practical application environment of the silica aerogel composites, the silica aerogel composites were treated single-side heat treatment at 400 ℃ for 1800 s, evaluating the stability of silica aerogel composites at 400 ℃ via the method of monitoring the quality loss ratio, size shrinkage ratio,, insulation properties, microstructure change .The results indicate that silica aerogel composites were exhibited excellent stability after single-side heat treatment 10 times, including the variations of mass loss, XYZ direction size shrinkage, thermal conductivity. The variation of elevated temperature and ambient temperature thermal conductivity and microstructure are very small. Comprehensively considering all properties of silica aerogel composites, it can reach up to 10 times.

    參考文獻
    相似文獻
    引證文獻
引用本文

陳茹,馮軍宗,姜勇剛,張忠明,馮堅.二氧化硅氣凝膠復(fù)合材料可重復(fù)使用性能研究[J].稀有金屬材料與工程,2018,47(S2):267~271.[CHEN Ru, FENG Junzong, JIANG Yonggang, ZHANG Zhongming, FENG Jian. The Research on Reusable Properties of Silica Aerogel Composites[J]. Rare Metal Materials and Engineering,2018,47(S2):267~271.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2017-12-22
  • 最后修改日期:2018-08-28
  • 錄用日期:2018-02-01
  • 在線發(fā)布日期: 2018-11-01
  • 出版日期: