4和P123為原料采用溶膠-凝膠法在不同條件下制備了介孔MnO2。研究了反應(yīng)物比和pH對催化劑結(jié)構(gòu)和催化降解性能的影響。溶膠-凝膠法制備介孔MnO2的最佳條件為：原料配比為10：1,pH值為7。合成材料的結(jié)構(gòu)和性能采用XRD、N2吸脫附、FT-IR的測試方法表征,結(jié)果表明P123和KMnO4合成的介孔MnO2具有較大的比表面積和孔徑,且有良好的HCHO催化降解性能。最后討論了介孔MnO2催化氧化HCHO的影響因素,發(fā)現(xiàn)在pH7 的情況下最有利于介孔MnO2的活性穩(wěn)定；在原料比為10：1情況下生成的介孔MnO2比表面積較大,催化降解性能較強(qiáng),在10h內(nèi)保持在對甲醛的降解率為95%以上。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
室溫下介孔MnO2降解低濃度甲醛的研究
作者:
作者單位:

1.中國計(jì)量大學(xué)材料科學(xué)與工程學(xué)院;2.材料科學(xué)與工程學(xué)院

作者簡介:

通訊作者:

中圖分類號:

基金項(xiàng)目:


Degradation of low concentration formaldehyde by mesoporous MnO2 at room temperature
Author:
Affiliation:

1.College of Materials Science and Engineering, China Jiliang University;2.College of Materials Science and Engineering, China Jiliang University, Hangzhou

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計(jì)
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    本文以KMnO4和P123為原料采用溶膠-凝膠法在不同條件下制備了介孔MnO2。研究了反應(yīng)物比和pH對催化劑結(jié)構(gòu)和催化降解性能的影響。溶膠-凝膠法制備介孔MnO2的最佳條件為：原料配比為10：1,pH值為7。合成材料的結(jié)構(gòu)和性能采用XRD、N2吸脫附、FT-IR的測試方法表征,結(jié)果表明P123和KMnO4合成的介孔MnO2具有較大的比表面積和孔徑,且有良好的HCHO催化降解性能。最后討論了介孔MnO2催化氧化HCHO的影響因素,發(fā)現(xiàn)在pH7 的情況下最有利于介孔MnO2的活性穩(wěn)定；在原料比為10：1情況下生成的介孔MnO2比表面積較大,催化降解性能較強(qiáng),在10h內(nèi)保持在對甲醛的降解率為95%以上。

    Abstract:

    Mesoporous MnO2 was prepared by sol-gel method using KMnO4 and P123. The structure and properties of the synthesized materials were characterized by XRD, N2 adsorption and desorption, and FT-IR. The effects of reactant ratio and pH on the catalytic oxidation performance of the product were investigated. The optimum conditions of the preparation were as follows: the ratio of KMnO4 and P123 was 10:1 and the pH was 7. The results shown that mesoporous MnO2 has good catalytic oxidation performance to HCHO. Finally, the influencing factors of the catalytic oxidation of HCHO by mesoporous MnO2 were discussed. The specific surface area of mesoporous MnO2 (pH7-10:1) was largest. The oxidation performance was the strongest, and the degradation rate of formaldehyde was maintained at 95 %.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

許凌亮,方建飛,湯惠睫,韓哲,金紅曉,葛洪良,王新慶,樓輝,金頂峰,彭曉領(lǐng),李靜,楊艷婷,洪波.室溫下介孔MnO2降解低濃度甲醛的研究[J].稀有金屬材料與工程,2020,49(4):1105~1109.[XU Ling-liang, FANG Jian-fei, TANG Hui-jie, HAN Zhe, JIN Hong-xiao, GE Hong-liang, WANG Xin-qing, LOU Hui, JIN Ding-feng, PENG Xiao-ling, LI Jing, YANG Yan-ting, HONG Bo. Degradation of low concentration formaldehyde by mesoporous MnO2 at room temperature[J]. Rare Metal Materials and Engineering,2020,49(4):1105~1109.]
DOI：10.12442/j. issn.1002-185X. SG20190065

復(fù)制
文章指標(biāo)
  • 點(diǎn)擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2019-04-26
  • 最后修改日期:2019-09-10
  • 錄用日期:2019-10-14
  • 在線發(fā)布日期: 2020-05-07
  • 出版日期: