2;納米管;水熱法;光催化"/> 2粉體在高濃度NaOH溶液中水熱反應(yīng)制備TiO2納米管,采用X射線衍射(XRD)、掃描電鏡(SEM),透射電鏡(TEM),紫外可見(jiàn)分光光度計(jì)(UV-Vis)考察了NaOH濃度、水熱反應(yīng)溫度、水熱反應(yīng)時(shí)間等因素對(duì)TiO2納米管結(jié)構(gòu)和性能的影響。結(jié)果表明：當(dāng)NaOH濃度為10mol/L,水熱反應(yīng)溫度為160℃,水熱反應(yīng)時(shí)間20h時(shí),所制備的TiO2納米管顯示出較高的光催化活性,經(jīng)紫外光照30min后,對(duì)甲基橙(MO)的降解率可達(dá)75.48%。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級(jí)檢索
水熱制備TiO2納米管及其光催化性能
DOI:
作者:
作者單位:

浙江大學(xué) 浙江加州國(guó)際納米技術(shù)研究院,浙江大學(xué) 材料科學(xué)與工程學(xué)院,浙江大學(xué) 材料科學(xué)與工程學(xué)院,浙江大學(xué) 材料科學(xué)與工程學(xué)院,浙江大學(xué) 浙江加州國(guó)際納米技術(shù)研究院,浙江大學(xué) 浙江加州國(guó)際納米技術(shù)研究院

作者簡(jiǎn)介:

通訊作者:

中圖分類(lèi)號(hào):

基金項(xiàng)目:

國(guó)家科技支撐計(jì)劃項(xiàng)目資助(項(xiàng)目號(hào)2013BAJ10B05)


Hydrothermal preparation of TiO2 nanotubes and its photocatalytic performance
Author:
Affiliation:

Zhejiang-California International NanoSystems Institute, Zhejiang University,,,,,Zhejiang-California International NanoSystems Institute, Zhejiang University

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問(wèn)統(tǒng)計(jì)
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評(píng)論
    摘要:

    本文利用TiO2粉體在高濃度NaOH溶液中水熱反應(yīng)制備TiO2納米管,采用X射線衍射(XRD)、掃描電鏡(SEM),透射電鏡(TEM),紫外可見(jiàn)分光光度計(jì)(UV-Vis)考察了NaOH濃度、水熱反應(yīng)溫度、水熱反應(yīng)時(shí)間等因素對(duì)TiO2納米管結(jié)構(gòu)和性能的影響。結(jié)果表明：當(dāng)NaOH濃度為10mol/L,水熱反應(yīng)溫度為160℃,水熱反應(yīng)時(shí)間20h時(shí),所制備的TiO2納米管顯示出較高的光催化活性,經(jīng)紫外光照30min后,對(duì)甲基橙(MO)的降解率可達(dá)75.48%。

    Abstract:

    TiO2 nanotubes were prepared through hydrothermal method with TiO2 power in high concentration NaOH solution. XRD, SEM, TEM and UV-Vis were adopted to analyze as-prepared TiO2 nanotubes. The influence of the factors, such as NaOH concentration, reaction time and temperature, on the structure and properties of TiO2 nanotubes were investigated. The results show that the uniform TiO2 nanotubes are obtained under optimum preparation conditions: 10mol/L of NaOH, 20h of reaction time and 160℃ of reaction temperature. TiO2 nanotubes exhibit higher photocatalytic activity, and the degradation rate of methyl orange (MO) in aqueous solution reached 75.48% after UV irradiation for 30 min.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

吳旭日,王輝,尤增宇,秦天,申乾宏,楊輝.水熱制備TiO2納米管及其光催化性能[J].稀有金屬材料與工程,2018,47(S2):26~30.[WU Xuri, WANG Hui, YOU Zengyu, QIN Tian, SHEN Qianhong, YANG Hui. Hydrothermal preparation of TiO2 nanotubes and its photocatalytic performance[J]. Rare Metal Materials and Engineering,2018,47(S2):26~30.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點(diǎn)擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2017-12-13
  • 最后修改日期:2018-02-05
  • 錄用日期:2018-02-07
  • 在線發(fā)布日期: 2018-11-01
  • 出版日期: