2納米多孔材料,使用酸堿兩步法催化,添加表面活性劑來降低溶劑的表面張力,從而減少樣品在干燥過程中的開裂。最后經過常壓老化干燥制備得到 SiO2納米多孔材料。制備得到的SiO2塊體密度為150~400mg/cm3,室內熱導率約為0.04~0.07W/(m.K)。這種方法制備的SiO2納米多孔材料大幅縮減制備成本,采用HCl作為酸性催化劑提高了工業(yè)生產安全,將很大程度上推動納米多孔材料的工業(yè)化生產和應用。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
水體系下兩步法SiO2納米多孔材料的制備與表征
DOI:
作者:
作者單位:

同濟大學 波爾固體物理研究所,同濟大學 波爾固體物理研究所

作者簡介:

通訊作者:

中圖分類號:

基金項目:

國家科技支撐項目(2013BAJ01B01)；上海市科委納米專項(12nm0503001)；科技部863項目(2013AA031801)


Preparation and characterization of SiO2 nano porous materials by two-steps approach in water system
Author:
Affiliation:

Pohl Institute of Solid State Physics,Tongji University,Pohl Institute of Solid State Physics,Tongji University

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    以去離子水為溶劑,低成本工業(yè)硅溶膠為硅源,在純水體系下制備低成本的SiO2納米多孔材料,使用酸堿兩步法催化,添加表面活性劑來降低溶劑的表面張力,從而減少樣品在干燥過程中的開裂。最后經過常壓老化干燥制備得到 SiO2納米多孔材料。制備得到的SiO2塊體密度為150~400mg/cm3,室內熱導率約為0.04~0.07W/(m.K)。這種方法制備的SiO2納米多孔材料大幅縮減制備成本,采用HCl作為酸性催化劑提高了工業(yè)生產安全,將很大程度上推動納米多孔材料的工業(yè)化生產和應用。

    Abstract:

    Nano porous material SiO2 were prepared by acid-alkali two steps approach with low cost industrial silica sol as silicon source and deionized water as solvent. The surfactant was used as the surface modifier to get rid of the broken of samples in the drying process. The densities, specific surface area and the average pore size of the obtained SiO2 monoliths are in the range of 150~400 mg/cm3 and the range of 0.04~0.07W/(m.K), respectively. This method greatly reduced the cost in the preparation of SiO2 nano porous material, which will largely promote the industrial production and application of porous SiO2 materials.

    參考文獻
    相似文獻
    引證文獻
引用本文

丁文慧,沈軍.水體系下兩步法SiO2納米多孔材料的制備與表征[J].稀有金屬材料與工程,2018,47(S2):79~83.[DING Wen-Hui, SHEN Jun. Preparation and characterization of SiO2 nano porous materials by two-steps approach in water system[J]. Rare Metal Materials and Engineering,2018,47(S2):79~83.]