Y2O3-MgO納米復(fù)相紅外透明陶瓷制備及其性能研究
作者:
作者單位:

1.天津市薄膜光學(xué)重點(diǎn)實(shí)驗(yàn)室;2.張家港匯普光學(xué)材料有限公司

作者簡介:

通訊作者:

中圖分類號:

TQ174

基金項(xiàng)目:

國家自然科學(xué)基金資助(項(xiàng)目號51702231)


Infrared-Transparent Y2O3-MgO Nanocomposite Fabricated and its Properties
Author:
Affiliation:

1.Tianjin Key Laboratory of Optical Thin Film,Tianjin Jinhang Technical Physics Institute,Tianjin;2.Zhangjiagang Huipu Optical Material Company,Suzhou

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計(jì)
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    以商用Y2O3、MgO納米粉體為原料，通過球磨混合方法制備了不同Y2O3/MgO配比的Y2O3-MgO納米復(fù)合粉體，使用X射線衍射、掃描電鏡、能量色散譜等表征手段對制備粉體的晶體結(jié)構(gòu)、形貌、成分以及均勻性進(jìn)行了表征。然后采用熱壓燒結(jié)方法制備Y2O3-MgO復(fù)相紅外透明陶瓷，使用紅外光譜儀，維氏硬度計(jì)等測試設(shè)備對復(fù)相透明陶瓷的光學(xué)和力學(xué)性能進(jìn)行了分析。重點(diǎn)研究了粉體配比、熱壓溫度、保溫和保壓時間等關(guān)鍵制備參數(shù)對Y2O3-MgO復(fù)相紅外透明陶瓷晶粒尺度、致密化程度、光學(xué)及力學(xué)性能的影響。并通過調(diào)控粉體制備工藝和熱壓燒結(jié)工藝，制備出了紅外透過率達(dá)到80%的Y2O3-MgO復(fù)相紅外透明陶瓷。同時在Y2O3：MgO = 1:1時，該復(fù)相陶瓷的硬度達(dá)到了12.3GPa。

    Abstract:

    Y2O3-MgO nanocomposite powders have been prepared by ball mill using the commercial Y2O3, MgO powders. The crystal structure, morphology, uniformity of the Y2O3-MgO nanocomposite powder have been characterized by XRD, SEM, EDS respectively. And then the hot-pressing has been used to densify of the Y2O3-MgO nanocomposite ceramic. The FTIR and Vickers hardness tester have been used to reveal the optical and mechanical properties of Y2O3-MgO nanocomposite ceramic with different preparation parameter. The transmittance and hardness reach to 80% (6μm) and 12.3 GPa respectively with optimal conditions.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

劉孟寅,張高峰,王躍忠,張彤,李霄鵬,甘碩文,張榮實(shí),褚建華. Y2O3-MgO納米復(fù)相紅外透明陶瓷制備及其性能研究[J].稀有金屬材料與工程,2020,49(2):718~722.[Mengyin Liu, Gaofeng Zhang, Yuezhong Wang, Tong Zhang, Xiaopeng Li, Shuowen Gan, Rongshi Zhang, Jianhua Chu. Infrared-Transparent Y2O3-MgO Nanocomposite Fabricated and its Properties[J]. Rare Metal Materials and Engineering,2020,49(2):718~722.]
DOI：10.12442/j. issn.1002-185X. QH20190017

復(fù)制
文章指標(biāo)
  • 點(diǎn)擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2019-03-10
  • 最后修改日期:2019-04-27
  • 錄用日期:2019-10-23
  • 在線發(fā)布日期: 2020-03-12
  • 出版日期: