孿晶界"/> 孿晶界的影響規(guī)律。結(jié)果表明，氫可以促進鑄態(tài)和鍛態(tài)合金γ相的靜態(tài)再結(jié)晶，并且再結(jié)晶程度隨氫含量的增加而增大；大量再結(jié)晶晶粒具有120o<111> 孿晶界，并揭示了120o<111> 孿晶界含量與氫含量的關(guān)系。氫致120o<111> 孿晶界增多的原因是氫減弱了γ相的彈性各向異性。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
TiAl基合金在置氫退火過程中γ相120o<111>孿晶界形成機制研究
作者:
作者單位:

1.濟南大學(xué);2.哈爾濱工業(yè)大學(xué)

作者簡介:

通訊作者:

中圖分類號:

基金項目:

國家自然科學(xué)基金項目（51275132, 51705199, 51372101），山東省自然科學(xué)基金項目（ZR2017BEE055），山東省優(yōu)秀中青年科學(xué)家獎勵基金（ZR2016EMB01），山東省泰山學(xué)者工程專項（2016-2020）


Investigation on the formation mechanism of 120o<111> twin boundaries in γ phase of a TiAl based alloy during annealing treatment in hydrogen atmosphere
Author:
Affiliation:

1.University of Jinan;2.Harbin Institute of Technology

Fund Project:

the National Natural Science Foundation of China (51275132, 51705199, 51372101), Shandong Provincial Natural Science Foundation, China (ZR2017BEE055),

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    本文利用金相顯微鏡、掃描電鏡、EBSD技術(shù)、透射電鏡和X射線衍射研究了鑄態(tài)和鍛態(tài)Ti–46Al–2V–1Cr–0.3Ni合金退火過程中氫對γ相120o<111>孿晶界的影響規(guī)律。結(jié)果表明，氫可以促進鑄態(tài)和鍛態(tài)合金γ相的靜態(tài)再結(jié)晶，并且再結(jié)晶程度隨氫含量的增加而增大；大量再結(jié)晶晶粒具有120o<111> 孿晶界，并揭示了120o<111> 孿晶界含量與氫含量的關(guān)系。氫致120o<111> 孿晶界增多的原因是氫減弱了γ相的彈性各向異性。

    Abstract:

    The effect of hydrogen on 120o<111> twin boundaries in γ phase of an as-cast and as-forged Ti–46Al–2V–1Cr–0.3Ni alloy was investigated by means of annealing treatment in hydrogen atmosphere, and the microstructure was observed by an optical microscopy, a scanning electron microscopy, an electron back scattered diffraction technique, a transmission electron microscopy and a X-ray diffraction apparatus. The results showed that hydrogen could promote γ-phase static recrystallization of the as-cast and as-forged alloy, and the extent of static recrystallization increased with increasing hydrogen content. Many static recrystallization grains possessed 120o<111> twin boundaries. The relationship between the fraction of 120o<111> twin boundaries and hydrogen content was given. Hydrogen-weakened γ-phase elastic anisotropy increased 120o<111> twin boundaries.

    參考文獻
    相似文獻
    引證文獻
引用本文

溫道勝,王守仁,單德彬,宗影影. TiAl基合金在置氫退火過程中γ相120o<111>孿晶界形成機制研究[J].稀有金屬材料與工程,2019,48(9):2789~2993.[Wen Daosheng, Wang Shouren, Shan Debin, Zong Yingying. Investigation on the formation mechanism of 120o<111> twin boundaries in γ phase of a TiAl based alloy during annealing treatment in hydrogen atmosphere[J]. Rare Metal Materials and Engineering,2019,48(9):2789~2993.]
DOI：10.12442/j. issn.1002-185X. E20180004

復(fù)制
文章指標(biāo)
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2018-02-03
  • 最后修改日期:2018-04-04
  • 錄用日期:2018-04-04
  • 在線發(fā)布日期: 2019-10-09
  • 出版日期: