2Al5層，該層延緩了其在熱浸鋁過程的失效。鋼材的再結(jié)晶對于熱浸鍍鋁過程中界面金屬間化合物的影響包括：（1）再結(jié)晶可降低IMCS的形核和生長能量，尤其是Fe4Al13相；（2）再結(jié)晶引起的晶粒沿密排方向排布可降低Al離子的擴散速率；（3）再結(jié)晶加劇了IMCS/鋼界面處的應(yīng)力失配，尤其是奧氏體鋼。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
再結(jié)晶對鋼在鋁液中形成的界面相穩(wěn)定性影響
作者:
作者單位:

1.東北大學(xué) 材料科學(xué)與工程學(xué)院，遼寧 沈陽 110819;2.西安稀有金屬材料研究院有限公司，陜西 西安 710016

作者簡介:

通訊作者:

中圖分類號:

基金項目:

陜西省自然科學(xué)基金青年項目No. 2022JQ-452；陜西省秦創(chuàng)原No. QCYRCXM-2022-189；稀有院院控課題K2206S


Effect of Recrystallization of Steel on Stability of Interme-tallic Phases in Molten Al
Author:
Affiliation:

1.School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China;2.Xi'an Rare Metal Materials Institute Co., Ltd, Xi 'an 710016, China

Fund Project:

Natural Science Foundation of Shaanxi Province (2022JQ-452); Qinchuangyuan Project of Shaanxi Province (QCYRCXM-2022-189); RMMI Research Project (K2206S)

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    研究了鋼的再結(jié)晶對熱浸鋁過程金屬間化合物（IMCS）層的穩(wěn)定性影響，結(jié)果表明：304不銹鋼在熱浸鍍過程的再結(jié)晶結(jié)構(gòu)重排造成該鋼材表面形成了非保護性IMCS層，該合金的腐蝕動力學(xué)滿足線性規(guī)律；再結(jié)晶程度較輕的410不銹鋼表面形成了穩(wěn)定且致密的Fe2Al5層，該層延緩了其在熱浸鋁過程的失效。鋼材的再結(jié)晶對于熱浸鍍鋁過程中界面金屬間化合物的影響包括：（1）再結(jié)晶可降低IMCS的形核和生長能量，尤其是Fe4Al13相；（2）再結(jié)晶引起的晶粒沿密排方向排布可降低Al離子的擴散速率；（3）再結(jié)晶加劇了IMCS/鋼界面處的應(yīng)力失配，尤其是奧氏體鋼。

    Abstract:

    The influence of steel's recrystallization on the stability of intermetallic compounds (IMCS) layer was investigated in molten Al at 700 °C. Results show that high degree of structural rearrangement leads to the formation of non-protective IMCS layer on the 304SS surface and its corrosion kinetics coincides with linear law. Compact and stable Fe2Al5 layer delays the failure of the 410SS in liquid Al. The stability of IMCS is affected by steel's recrystallization in three aspects: (1) energy for IMCS nucleation and growth are reduced, especially for Fe4Al13; (2) grain orientation transforms to close-packed direction which slows down the diffusion rate of Al ion; (3) stress mismatch is increased at the IMCS/steel interface, especially for the austenitic 304SS.

    參考文獻
    相似文獻
    引證文獻
引用本文

張佳銳,余中狄,吳金平.再結(jié)晶對鋼在鋁液中形成的界面相穩(wěn)定性影響[J].稀有金屬材料與工程,2023,52(12):4065~4072.[Zhang Jiarui, Yu Zhongdi, Wu Jinping. Effect of Recrystallization of Steel on Stability of Interme-tallic Phases in Molten Al[J]. Rare Metal Materials and Engineering,2023,52(12):4065~4072.]
DOI：10.12442/j. issn.1002-185X.20230258

復(fù)制
文章指標(biāo)
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2023-05-01
  • 最后修改日期:2023-06-20
  • 錄用日期:2023-06-28
  • 在線發(fā)布日期: 2023-12-25
  • 出版日期: 2023-12-22