2B4O7、H3BO3、KF或KHF2組成）去除304不銹鋼表面氧化膜，研究了銀釬劑對304不銹鋼表面氧化膜的去除機理。結果表明，700 ℃時，在釬劑成分中某一成分的單獨作用下，K2B4O7和KF不能去除304不銹鋼表面氧化膜；在任意2種成分的協(xié)同作用下，只有K2B4O7與H3BO3的混合物在700 ℃下不能熔化，其余二元混合物均能與鋼板表面氧化物反應；自由能（ΔGmθ）和反應平衡常數(shù)（Kθ）的計算結果顯示，釬劑去除氧化膜的主要原因是該過程中釬劑中的F替代氧化物中的O，該反應的平衡常數(shù)達到 1.3×10167，自由能小于零，反應可以進行。XRD結果顯示，在2θ=18°位置的峰形發(fā)生改變，說明KF被KHF2替代后，釬劑去除氧化膜的機理發(fā)生變化。含有KF和KHF2的3號釬劑在540 ℃時可以有效去除鋼板表面氧化膜，與釬劑的反應產(chǎn)物具有非晶結構特征。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
含氟化物銀釬劑去除304不銹鋼表面氧化膜的機理
作者:
作者單位:

1.鄭州機械研究所 新型釬焊材料與技術國家重點實驗室，河南 鄭州 450001;2.中機智能裝備創(chuàng)新研究院(寧波)，浙江 寧波 315700

作者簡介:

通訊作者:

中圖分類號:

基金項目:

國家自然科學基金項目（面上項目，重點項目，重大項目）（U2004186）


Removal Mechanism of Oxide Film on 304 Stainless Steel Surface by Silver Brazing Flux Containing Fluoride
Author:
Affiliation:

1.State Key Laboratory of Advanced Brazing Filler Metals and Technology, Zhengzhou Research Institute of Mechanical Engineering Co., Ltd, Zhengzhou 450001, China;2.China Innovation Academy of Intelligent Equipment (Ningbo) Co., Ltd, Ningbo 315700, China

Fund Project:

National Natural Science Foundation of China (U2004186)

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    使用銀釬劑（由K2B4O7、H3BO3、KF或KHF2組成）去除304不銹鋼表面氧化膜，研究了銀釬劑對304不銹鋼表面氧化膜的去除機理。結果表明，700 ℃時，在釬劑成分中某一成分的單獨作用下，K2B4O7和KF不能去除304不銹鋼表面氧化膜；在任意2種成分的協(xié)同作用下，只有K2B4O7與H3BO3的混合物在700 ℃下不能熔化，其余二元混合物均能與鋼板表面氧化物反應；自由能（ΔGmθ）和反應平衡常數(shù)（Kθ）的計算結果顯示，釬劑去除氧化膜的主要原因是該過程中釬劑中的F替代氧化物中的O，該反應的平衡常數(shù)達到 1.3×10167，自由能小于零，反應可以進行。XRD結果顯示，在2θ=18°位置的峰形發(fā)生改變，說明KF被KHF2替代后，釬劑去除氧化膜的機理發(fā)生變化。含有KF和KHF2的3號釬劑在540 ℃時可以有效去除鋼板表面氧化膜，與釬劑的反應產(chǎn)物具有非晶結構特征。

    Abstract:

    Silver brazing flux, composed of K2B4O7, H3BO3, KF and/or KHF2, was used to remove the oxide film on the surface of 304 stainless steel. The oxide film removal mechanism was studied. The results show that K2B4O7 and KF cannot remove the oxide film on the surface of 304 stainless steel at 700 °C. Under the synergistic action of any two components, only the mixture of K2B4O7 and H3BO3 cannot melt at 700 °C. The calculation results of the reaction equilibrium constant (Kθ) and Gibbs free energy (△Gmθ) show that the main reason for removing oxide film is that F in the brazing flux can replace O in the oxide in the process. XRD results show that the peak pattern at 2θ=18° is changed, indicating that the mechanism of removing oxide film is different when KF is replaced by KHF2 in silver brazing flux. No. 3 brazing flux with both KF and KHF2 can effectively remove the oxide film on the surface of the 304 stainless steel plate at 540 °C. The reaction product has the characteristics of amorphous structure.

    參考文獻
    相似文獻
    引證文獻
引用本文

趙月,龍偉民,黃森,鐘素娟,沈元勛,王路乙.含氟化物銀釬劑去除304不銹鋼表面氧化膜的機理[J].稀有金屬材料與工程,2022,51(12):4502~4507.[Zhao Yue, Long Weimin, Huang Sen, Zhong Sujuan, Shen Yuanxun, Wang Luyi. Removal Mechanism of Oxide Film on 304 Stainless Steel Surface by Silver Brazing Flux Containing Fluoride[J]. Rare Metal Materials and Engineering,2022,51(12):4502~4507.]
DOI：10.12442/j. issn.1002-185X.20220102

復制
文章指標
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2022-02-09
  • 最后修改日期:2022-12-02
  • 錄用日期:2022-03-28
  • 在線發(fā)布日期: 2023-01-11
  • 出版日期: 2022-12-30