3BO3、K2B4O7和KF（質量比為7:10:3）3種組分配制而成的銀釬劑的去膜機理。結果表明：在700 ℃時，K2B4O7或KF都不能單獨去除Q235鋼板表面的氧化膜，且KF會加快高溫下鋼表面的氧化速率；H3BO3能夠去除Q235鋼表面的氧化膜，然而其反應產物具有明顯的非晶結構特征，并且流動性差。此外在700 ℃時，H3BO3與KF能夠發(fā)生反應，其反應產物可以去除鋼表面氧化膜。KF和K2B4O7之間也能在700 ℃發(fā)生類似的反應，然而其反應產物非常堅硬。因此，在700 ℃時，H3BO3、K2B4O7和KF混合釬劑能夠與Q235鋼板表面氧化膜反應，且反應產物具有明顯的非晶特征。KF的加入將非反應性H3BO3-K2B4O7二元體系轉化為反應性KF-H3BO3-K2B4O7三元體系。在這個三元體系中，KF不但對鋼板沒有腐蝕性，反而促進了氧化膜的去除。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
FB3-F銀釬劑去膜機理
作者:
作者單位:

1.鄭州機械研究所 新型釬焊材料與技術國家重點實驗室，河南 鄭州 450001;2.中機智能裝備創(chuàng)新研究院(寧波)，浙江 寧波 315700

作者簡介:

通訊作者:

中圖分類號:

基金項目:

國家自然科學基金項目（面上項目，重點項目，重大項目）(U2004186)；鄭州市重大科技創(chuàng)新專項資助項目（2019CXZX0065)


Film Removal Mechanism of FB3-F Silver Brazing Flux
Author:
Affiliation:

1.State Key Laboratory of Advanced Brazing Filler Metals and Technology, Zhengzhou Research Institute of Mechanical Engineering Co., Ltd, Zhengzhou 450001, China;2.China Innovation Academy of Intelligent Equipment (Ningbo) Co., Ltd, Ningbo 315700, China

Fund Project:

National Natural Science Foundation of China (U2004186); Special Support Project for Major Scientific and Technological Innovation in Zhengzhou (2019CXZX0065)

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    研究了由H3BO3、K2B4O7和KF（質量比為7:10:3）3種組分配制而成的銀釬劑的去膜機理。結果表明：在700 ℃時，K2B4O7或KF都不能單獨去除Q235鋼板表面的氧化膜，且KF會加快高溫下鋼表面的氧化速率；H3BO3能夠去除Q235鋼表面的氧化膜，然而其反應產物具有明顯的非晶結構特征，并且流動性差。此外在700 ℃時，H3BO3與KF能夠發(fā)生反應，其反應產物可以去除鋼表面氧化膜。KF和K2B4O7之間也能在700 ℃發(fā)生類似的反應，然而其反應產物非常堅硬。因此，在700 ℃時，H3BO3、K2B4O7和KF混合釬劑能夠與Q235鋼板表面氧化膜反應，且反應產物具有明顯的非晶特征。KF的加入將非反應性H3BO3-K2B4O7二元體系轉化為反應性KF-H3BO3-K2B4O7三元體系。在這個三元體系中，KF不但對鋼板沒有腐蝕性，反而促進了氧化膜的去除。

    Abstract:

    The film removal mechanism of FB3-F silver brazing flux consisting of H3BO3, K2B4O7, and KF with the mass ratio of 7:10:3 was studied. Results show that K2B4O7 or KF cannot individually remove the oxide film on Q235 steel at 700 °C, and KF even accelerates the oxidation rate of steel surface at high temperature. H3BO3 can remove the oxide film at 700 °C, but the product possesses an obvious amorphous structure feature and poor fluidity. Furthermore, H3BO3 can react with KF at 700 °C, and the reaction product can remove the oxide film. Similarly, K2B4O7 can react with KF, but the product is hard. The mixture solder consisting of H3BO3, K2B4O7, and KF can react with the oxide film on surface of Q235 steel plate, and the reaction product presents obvious amorphous feature. The addition of KF transforms the nonreactive H3BO3-K2B4O7 binary system into the reactive KF-H3BO3-K2B4O7 ternary system at 700 °C. KF shows no corrosivity and promotes the removal of oxide film of steel plates in this ternary system.

    參考文獻
    相似文獻
    引證文獻
引用本文

趙月,龍偉民,黃森,鐘素娟,沈元勛,王路乙.FB3-F銀釬劑去膜機理[J].稀有金屬材料與工程,2021,50(11):3857~3861.[Zhao Yue, Long Weimin, Huang Sen, Zhong Sujuan, Shen Yuanxun, Wang Luyi. Film Removal Mechanism of FB3-F Silver Brazing Flux[J]. Rare Metal Materials and Engineering,2021,50(11):3857~3861.]
DOI：10.12442/j. issn.1002-185X.20210231

復制
文章指標
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2021-03-19
  • 最后修改日期:2021-04-08
  • 錄用日期:2021-05-13
  • 在線發(fā)布日期: 2021-11-25
  • 出版日期: 2021-11-24