2熔鹽中進(jìn)行電脫氧，制備了CoCrFeNi高熵合金。通過X射線衍射（XRD）、掃描電子顯微鏡（SEM）和能量色散X射線能譜（EDS）研究了不同電解時間下金屬氧化物轉(zhuǎn)化為高熵合金的相變過程。結(jié)果表明，CoCrFeNi高熵合金的形成過程包括快速脫氧和深度脫氧2個階段。在快速脫氧階段，在1 h內(nèi)去除了燒結(jié)氧化物球團(tuán)中93.93%（質(zhì)量分?jǐn)?shù)）的氧，電流效率達(dá)到89.95%。電解結(jié)束后，產(chǎn)物的氧含量可達(dá)0.26%（質(zhì)量分?jǐn)?shù)），電流效率為17.93%。該高熵合金的形成過程可用于指導(dǎo)建立低成本、高效率的電化學(xué)路線。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
CoCrFeNi高熵合金在金屬氧化物熔鹽電脫氧中的形成過程
作者:
作者單位:

1.重慶大學(xué) 材料科學(xué)與工程學(xué)院，重慶 400044;2.重慶大學(xué) 釩鈦冶金與新材料重慶市重點實驗室，重慶 400044

作者簡介:

通訊作者:

中圖分類號:

基金項目:

國家自然科學(xué)基金項目（面上項目，重點項目，重大項目）


Formation Process of CoCrFeNi High Entropy Alloy via Electro-Deoxidization of Metal Oxides in Molten Salt
Author:
Affiliation:

1.College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China;2.Chongqing Key Laboratory of Vanadium-Titanium Metallurgy and New Materials, Chongqing University, Chongqing 400044, China

Fund Project:

National Natural Science Foundation of China (51674054)

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    在1173 K下將金屬氧化物在CaCl2熔鹽中進(jìn)行電脫氧，制備了CoCrFeNi高熵合金。通過X射線衍射（XRD）、掃描電子顯微鏡（SEM）和能量色散X射線能譜（EDS）研究了不同電解時間下金屬氧化物轉(zhuǎn)化為高熵合金的相變過程。結(jié)果表明，CoCrFeNi高熵合金的形成過程包括快速脫氧和深度脫氧2個階段。在快速脫氧階段，在1 h內(nèi)去除了燒結(jié)氧化物球團(tuán)中93.93%（質(zhì)量分?jǐn)?shù)）的氧，電流效率達(dá)到89.95%。電解結(jié)束后，產(chǎn)物的氧含量可達(dá)0.26%（質(zhì)量分?jǐn)?shù)），電流效率為17.93%。該高熵合金的形成過程可用于指導(dǎo)建立低成本、高效率的電化學(xué)路線。

    Abstract:

    CoCrFeNi high entropy alloys (HEAs) were prepared by electro-deoxidization of metal oxides in CaCl2 molten salt at 1173 K. The phase transformation from the metal oxides to HEA under different electrolysis durations was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS). The results show that the formation process of CoCrFeNi HEA includes two stages: the rapid deoxidization stage and deep deoxidization stage. In the rapid deoxidization stage, 93.93wt% oxygen in sintered oxide pellet is removed within 1 h and the current efficiency reaches 89.95%. After electrolysis of 15 h, the oxygen content of the product is 0.26wt% and the current efficiency is 17.93%. The formation process of CoCrFeNi HEA provides guidance for establishing the electrochemical route with low cost and high efficiency.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

楊宇,羅翔宇,馬通祥,胡麗文,溫良英,扈玫瓏.CoCrFeNi高熵合金在金屬氧化物熔鹽電脫氧中的形成過程[J].稀有金屬材料與工程,2021,50(9):3116~3124.[Yang Yu, Luo Xiangyu, Ma Tongxiang, Hu Liwen, Wen Liangying, Hu Meilong. Formation Process of CoCrFeNi High Entropy Alloy via Electro-Deoxidization of Metal Oxides in Molten Salt[J]. Rare Metal Materials and Engineering,2021,50(9):3116~3124.]
DOI：10.12442/j. issn.1002-185X.20200548

復(fù)制
文章指標(biāo)
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2020-07-28
  • 最后修改日期:2020-08-25
  • 錄用日期:2020-09-02
  • 在線發(fā)布日期: 2021-09-26
  • 出版日期: 2021-09-24