2O3/Al-10Si復(fù)合材料,并分別在160 ℃保溫2、4、6 h的條件下研究了高壓凝固Al2O3/Al-10Si復(fù)合材料的組織熱穩(wěn)定性以及力學性能轉(zhuǎn)變規(guī)律。研究表明：熱處理導(dǎo)致高壓凝固Al2O3/Al-10Si復(fù)合材料α相固溶的Si在熱激活的作用下脫溶析出,聚集長大形成細小顆粒彌散分布于α相內(nèi),形成沉淀強化；160 ℃熱處理后α相固溶的Si析出,過飽和程度下降,材料性能逐漸趨于穩(wěn)定,在沉淀強化的共同作用下,Al2O3/Al-10Si復(fù)合材料抗壓強度和壓縮率較熱處理前均有所上升。而160℃保溫4 h的條件下,材料的綜合力學性能最好。尤其在5 GPa壓力下凝固的Al2O3/Al-10Si復(fù)合材料,抗壓強度可達到716 MPa。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
高壓凝固Al2O3/Al-10Si復(fù)合材料組織熱穩(wěn)定性及力學性能研究
作者:
作者單位:

1.安徽工程大學;2.衢州學院

作者簡介:

通訊作者:

中圖分類號:

基金項目:

浙江省自然科學基金(LY18E010003,LQ20E010003)；國家自然科學基金(51801112,51501100,51704001,)；


Effect of Heat Treatment on Thermal Stability of Microstructure and Mechanical Properties of High Pressure Solidified Al2O3/Al-10Si
Author:
Affiliation:

1.School of Mechanical and Automotive Engineering,Anhui polytechnic University;2.School of Mechanical Engineering Key Laboratory of Air-driven Equipment Technology of Zhejiang Province,Quzhou University

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    本文采用高壓凝固的方法分別在3、4、5 GPa的壓力下制備了Al2O3/Al-10Si復(fù)合材料,并分別在160 ℃保溫2、4、6 h的條件下研究了高壓凝固Al2O3/Al-10Si復(fù)合材料的組織熱穩(wěn)定性以及力學性能轉(zhuǎn)變規(guī)律。研究表明：熱處理導(dǎo)致高壓凝固Al2O3/Al-10Si復(fù)合材料α相固溶的Si在熱激活的作用下脫溶析出,聚集長大形成細小顆粒彌散分布于α相內(nèi),形成沉淀強化；160 ℃熱處理后α相固溶的Si析出,過飽和程度下降,材料性能逐漸趨于穩(wěn)定,在沉淀強化的共同作用下,Al2O3/Al-10Si復(fù)合材料抗壓強度和壓縮率較熱處理前均有所上升。而160℃保溫4 h的條件下,材料的綜合力學性能最好。尤其在5 GPa壓力下凝固的Al2O3/Al-10Si復(fù)合材料,抗壓強度可達到716 MPa。

    Abstract:

    Al2O3/Al-10Si composites were prepared by high pressure solidification at 3, 4, 5 GPa, and then heat treated at 160 °C for 2, 4, and 6 h. Thermal stability of microstructure and mechanical properties of Al2O3/Al-10Si composites under high pressure were systematically studied. The results showed that heat treatment leads to the precipitation of Si particles due to the supersaturation in α phase.The precipitation of Si leads to a decrease of supersaturation. The compression strength and ration shows a slight increase after heat treatment due to the combination of precipitation strengthening and solid solution strengthening. At 160℃/4h, Al2O3/Al-10Si composites showed the best mechanical properties. After solidified under 5GPa and heat treatment at 160℃/4h, Al2O3/Al-10Si composites got the maximum compressive strength which is about 716MPa.

    參考文獻
    相似文獻
    引證文獻
引用本文

朱冬冬,陳志鵬,王剛,董多,王曉紅,張艷衡.高壓凝固Al2O3/Al-10Si復(fù)合材料組織熱穩(wěn)定性及力學性能研究[J].稀有金屬材料與工程,2020,49(9):3260~3264.[Zhu Dongdong, Chen Zhipeng, Wang Gang, Dong Duo, Wang Xiaohong, Zhang Yanheng. Effect of Heat Treatment on Thermal Stability of Microstructure and Mechanical Properties of High Pressure Solidified Al2O3/Al-10Si[J]. Rare Metal Materials and Engineering,2020,49(9):3260~3264.]
DOI：10.12442/j. issn.1002-185X.20200071

復(fù)制
文章指標
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2020-02-07
  • 最后修改日期:2020-04-28
  • 錄用日期:2020-05-08
  • 在線發(fā)布日期: 2020-10-15
  • 出版日期: