4C鋁基管材;界面結(jié)合;"/> 4C顆粒含量為10wt.%的鋁基復(fù)合材料管材,研究了變形量對復(fù)合管材微觀組織和力學(xué)性能的影響。 研究結(jié)果表明:隨著旋壓變形量的增加,B4C鋁基復(fù)合管材內(nèi)部B4C顆粒分布由類似網(wǎng)狀結(jié)構(gòu)變?yōu)榫鶆蚍植?B4C顆粒與基體鋁合金之間界面形成了冶金結(jié)合；等離子放電燒結(jié)過程中的顆粒之間的“尖端放電”效應(yīng)使得顆粒之間的界面處產(chǎn)生局部高溫,促進了界面之間的結(jié)合,在界面處產(chǎn)生了AlB2和Al3BC金屬間化合物；旋壓變形量的增加,細化了鋁合金的晶粒尺寸,減小了B4C的顆粒尺寸,但旋壓過程中導(dǎo)致的大尺寸B4C顆粒的斷裂弱化了細晶強化和顆粒強化對抗拉強度的作用。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
旋壓變形量對B4C增強鋁基復(fù)合管微觀組織及力學(xué)性能的影響
作者:
作者單位:

太原理工大學(xué) 山西省鎂基重點實驗室 新材料界面科學(xué)與工程省部共建教育部重點實驗室 山西 太原

作者簡介:

通訊作者:

中圖分類號:

TG77

基金項目:

國家自然科學(xué)基金資助(項目號51805358、51775366),博士后基金資助(項目號2018M631773)


Influence of spinning deformation on microstructures and tensile properties ofB4C particulate reinforced aluminium matrix composite tube
Author:
Affiliation:

Taiyuan University of Technology

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    本文采用等離子放電燒結(jié)+異步錯距旋壓方法制備了不同旋壓變形量的B4C顆粒含量為10wt.%的鋁基復(fù)合材料管材,研究了變形量對復(fù)合管材微觀組織和力學(xué)性能的影響。 研究結(jié)果表明:隨著旋壓變形量的增加,B4C鋁基復(fù)合管材內(nèi)部B4C顆粒分布由類似網(wǎng)狀結(jié)構(gòu)變?yōu)榫鶆蚍植?B4C顆粒與基體鋁合金之間界面形成了冶金結(jié)合；等離子放電燒結(jié)過程中的顆粒之間的“尖端放電”效應(yīng)使得顆粒之間的界面處產(chǎn)生局部高溫,促進了界面之間的結(jié)合,在界面處產(chǎn)生了AlB2和Al3BC金屬間化合物；旋壓變形量的增加,細化了鋁合金的晶粒尺寸,減小了B4C的顆粒尺寸,但旋壓過程中導(dǎo)致的大尺寸B4C顆粒的斷裂弱化了細晶強化和顆粒強化對抗拉強度的作用。

    Abstract:

    In this study,the B4C particles reinforced aluminium matrix composite tube with different deformation was first fabricated by spark plasma sintering (SPS) and followed by asynchronous offset spinning. It was found that the B4C particles distributed change from net to relatively homogeneously in the aluminium matrix with the spun deformation increase. The interface between B4C and aluminium was formatted metallurgical bonding due to the discharge was happened lead to the local high temperature existed during SPS processing and the interface was mainly consisted of AlB2 and Al3BC phase. With the deformation increasing, the aluminium grain and B4C size was decrease. But, large size of B4C particles fracture was decrease the fine-grain and particles strengthening function for the tensile strengthening.

    參考文獻
    相似文獻
    引證文獻
引用本文

陳洪勝,王文先,聶慧慧,張鵬,劉潤愛,楊濤,張媛琦.旋壓變形量對B4C增強鋁基復(fù)合管微觀組織及力學(xué)性能的影響[J].稀有金屬材料與工程,2019,48(9):2923~2929.[chenhongsheng, Wangwenxian, niehuihui, zhangpeng, liurunai, Yang Tao, Zhang Yuanqi. Influence of spinning deformation on microstructures and tensile properties ofB4C particulate reinforced aluminium matrix composite tube[J]. Rare Metal Materials and Engineering,2019,48(9):2923~2929.]
DOI：10.12442/j. issn.1002-185X.20181131

復(fù)制
文章指標(biāo)
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2018-11-11
  • 最后修改日期:2018-12-27
  • 錄用日期:2019-02-21
  • 在線發(fā)布日期: 2019-10-09
  • 出版日期: