3–LiF–BaF2; CeO2; 電沉積"/> 2在CeF3–LiF–BaF2熔鹽中的溶解機理,并采用鉬金屬電極研究了生成的Ce(III)在CeF3–LiF–BaF2熔鹽中的電化學行為。通過循環(huán)伏安曲線、計時電流法、恒電位電解法研究了Ce(III)的電解還原機理,并采用XRD、SEM、EDS對溶解反應產(chǎn)物和電解產(chǎn)物進行了物相、成分和微觀組織分析。結(jié)果表明：CeO2通過可與CeF3反應生成CeOF進而溶解于CeF3–LiF–BaF2熔鹽中,CeOF可被直接電解還原生成金屬Ce,Ce(III)在Mo電極上的電化學反應是一個單步的三電子可逆過程,反應受擴散控制。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
CeO2在CeF3–LiF–BaF2熔鹽中的溶解過程及電化學行為研究
作者:
作者單位:

1.東北大學冶金學院;2.東北大學材料電磁過程研究教育部重點實驗室

作者簡介:

通訊作者:

中圖分類號:

基金項目:


The dissolution and electrochemical behaviour of CeO2 in molten CeF3–LiF–BaF2
Author:
Affiliation:

1.School of Metallurgy, Northeastern University;2.School of Metallurgy,Northeastern University

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    本文研究了CeO2在CeF3–LiF–BaF2熔鹽中的溶解機理,并采用鉬金屬電極研究了生成的Ce(III)在CeF3–LiF–BaF2熔鹽中的電化學行為。通過循環(huán)伏安曲線、計時電流法、恒電位電解法研究了Ce(III)的電解還原機理,并采用XRD、SEM、EDS對溶解反應產(chǎn)物和電解產(chǎn)物進行了物相、成分和微觀組織分析。結(jié)果表明：CeO2通過可與CeF3反應生成CeOF進而溶解于CeF3–LiF–BaF2熔鹽中,CeOF可被直接電解還原生成金屬Ce,Ce(III)在Mo電極上的電化學反應是一個單步的三電子可逆過程,反應受擴散控制。

    Abstract:

    The dissolution mechanism of CeO2 in molten CeF3–LiF–BaF2 and the electrochemical behavior of Ce(III) on molybdenum electrode in molten CeF3–LiF–BaF2 were investigated. Cyclic voltammetry, chronoamperometry and potentiostatic electrolysis were performed to investigate the reduction mechanism of Ce(III) ions. The products obtained by dissolution reaction and potentiostatic electrolysis were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS). The results show that CeO2 can dissolve into the fluoride molten salts in the form of CeOF, by reacting with CeF3. Further, cerium oxyfluorides can be directly reduced to cerium metal with a purity of 99.38–99.81 wt% on molybdenum electrode via a reversible three-electron-transfer process, which is controlled by diffusion.

    參考文獻
    相似文獻
    引證文獻
引用本文

李斌川,李師居,孔亞鵬,陳建設(shè),劉奎仁,韓慶. CeO2在CeF3–LiF–BaF2熔鹽中的溶解過程及電化學行為研究[J].稀有金屬材料與工程,2020,49(3):749~754.[Li Binchuan, Li Shiju, Kong Yapeng, Chen Jianshe, Liu Kuiren, Han Qing. The dissolution and electrochemical behaviour of CeO2 in molten CeF3–LiF–BaF2[J]. Rare Metal Materials and Engineering,2020,49(3):749~754.]
DOI：10.12442/j. issn.1002-185X.20181104

復制
文章指標
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2018-10-30
  • 最后修改日期:2018-11-26
  • 錄用日期:2018-12-05
  • 在線發(fā)布日期: 2020-04-08
  • 出版日期: