3Zr-η′核殼顆粒。結(jié)果發(fā)現(xiàn)：Al3Zr顆粒在合金基體中以兩種形態(tài)存在,一種是與基體共格的單獨存在的Al3Zr顆粒；另外一種是作為η′析出相形核位置的核心Al3Zr顆粒,形成了一種與基體半共格的Al3Zr-η′核殼顆粒。該核殼顆粒的殼層由四種η′析出相變體組成。核心Al3Zr顆粒內(nèi)部的晶格變形低于單獨存在的Al3Zr顆粒,η′析出相和基體界面處存在顯著的晶格應(yīng)變。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
Al-Zn-Mg-Cu合金中一種新型Al3Zr-η′核殼顆粒的透射電子顯微鏡觀察
DOI:
作者:
作者單位:

內(nèi)蒙古工業(yè)大學(xué)材料科學(xué)與工程學(xué)院

作者簡介:

通訊作者:

中圖分類號:

基金項目:

國家自然科學(xué)基金項目（面上項目，重點項目，重大項目）,國家教育部博士點基金


Transmission Electron Microscopic Observation of a Novel Al3Zr-η′ Core-shell Particle in Al-Zn-Mg-Cu Alloy
Author:
Affiliation:

College of Materials Science and Engineering,Inner Mongolia University of Technology

Fund Project:

The National Natural Science Foundation of China,Ph.D. Programs Foundation of the Ministry of Education of China

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    利用高分辨透射電子顯微鏡和電子衍射觀察了Al-12Zn-2.4Mg-1.1Cu-0.5Ni-0.2Zr合金中的Al3Zr-η′核殼顆粒。結(jié)果發(fā)現(xiàn)：Al3Zr顆粒在合金基體中以兩種形態(tài)存在,一種是與基體共格的單獨存在的Al3Zr顆粒；另外一種是作為η′析出相形核位置的核心Al3Zr顆粒,形成了一種與基體半共格的Al3Zr-η′核殼顆粒。該核殼顆粒的殼層由四種η′析出相變體組成。核心Al3Zr顆粒內(nèi)部的晶格變形低于單獨存在的Al3Zr顆粒,η′析出相和基體界面處存在顯著的晶格應(yīng)變。

    Abstract:

    The Al3Zr-η′ core-shell particles were observed in the Al-12Zn-2.4Mg-1.1Cu-0.5Ni-0.2Zr alloy using high-resolution transmission electron microscopy and electron diffraction. Two types of Al3Zr particles appeared in the Al matrix: one a standalone Al3Zr particle coherent with the matrix and the other an as-core Al3Zr particle acting as nucleation for η′ precipitates resulting in a core-shell particle which is semi-coherent with the matrix. The shell is composed of η′ precipitates with four variants. The strain in as-core Al3Zr is lower than the standalone, and a considerable amount of strain exists across the interfacial regions between the η′ precipitates and the matrix.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

劉飛,白樸存,侯小虎,佟乃強,崔曉明. Al-Zn-Mg-Cu合金中一種新型Al3Zr-η′核殼顆粒的透射電子顯微鏡觀察[J].稀有金屬材料與工程,2018,47(11):3272~3276.[Fei Liu, Pucun Bai, Xiaohu Hou, Naiqiang Tong, Xiaoming Cui. Transmission Electron Microscopic Observation of a Novel Al3Zr-η′ Core-shell Particle in Al-Zn-Mg-Cu Alloy[J]. Rare Metal Materials and Engineering,2018,47(11):3272~3276.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2017-03-08
  • 最后修改日期:2017-05-04
  • 錄用日期:2017-05-16
  • 在線發(fā)布日期: 2018-12-19
  • 出版日期: