4Cp/6061Al復(fù)合材料; 動態(tài)再結(jié)晶; 臨界條件; 加工硬化率"/> 4Cp/6061Al復(fù)合材料的熱變形行為和動態(tài)再結(jié)晶臨界條件進行了研究,采用的溫度范圍為350℃-500℃,應(yīng)變速率范圍為0.001s-1-1s-1。應(yīng)力-應(yīng)變曲線顯示動態(tài)再結(jié)晶是復(fù)合材料熱變形過程中主要的軟化機制,并利用峰值應(yīng)力構(gòu)建了基于Arrhenius形式的本構(gòu)方程?；诩庸び不是€,求解了表示動態(tài)再結(jié)晶發(fā)生的臨界應(yīng)變與臨界應(yīng)力值。結(jié)果表明,臨界應(yīng)力與峰值應(yīng)力存在線性關(guān)系：σc=0.8374σp-0.33708。此外,引入Zener-Hollomon 參數(shù)描述變形條件對臨界條件的影響,得到臨界應(yīng)變與Z參數(shù)的關(guān)系：εc=2.39×10-4Z0.11022。最后,通過θ-ε曲線得到了復(fù)合材料完成動態(tài)再結(jié)晶時的穩(wěn)態(tài)應(yīng)變,并繪制了動態(tài)再結(jié)晶圖。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
B4Cp/6061Al復(fù)合材料動態(tài)再結(jié)晶臨界條件
DOI:
作者:
作者單位:

北京有色金屬研究總院,北京有色金屬研究總院,北京有色金屬研究總院

作者簡介:

通訊作者:

中圖分類號:

基金項目:

國家自然科學(xué)基金項目（面上項目，重點項目，重大項目）


Critical Conditions of Dynamic Recrystallization for B4Cp/6061Al composite
Author:
Affiliation:

General Research Institute of Non-ferrous Metals,General Research Institute of Non-ferrous Metals,General Research Institute of Non-ferrous Metals

Fund Project:

The National Natural Science Foundation of China (General Program, Key Program, Major Research Plan)

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    通過等溫?zé)釅嚎s實驗對25vol.% B4Cp/6061Al復(fù)合材料的熱變形行為和動態(tài)再結(jié)晶臨界條件進行了研究,采用的溫度范圍為350℃-500℃,應(yīng)變速率范圍為0.001s-1-1s-1。應(yīng)力-應(yīng)變曲線顯示動態(tài)再結(jié)晶是復(fù)合材料熱變形過程中主要的軟化機制,并利用峰值應(yīng)力構(gòu)建了基于Arrhenius形式的本構(gòu)方程。基于加工硬化率曲線,求解了表示動態(tài)再結(jié)晶發(fā)生的臨界應(yīng)變與臨界應(yīng)力值。結(jié)果表明,臨界應(yīng)力與峰值應(yīng)力存在線性關(guān)系：σc=0.8374σp-0.33708。此外,引入Zener-Hollomon 參數(shù)描述變形條件對臨界條件的影響,得到臨界應(yīng)變與Z參數(shù)的關(guān)系：εc=2.39×10-4Z0.11022。最后,通過θ-ε曲線得到了復(fù)合材料完成動態(tài)再結(jié)晶時的穩(wěn)態(tài)應(yīng)變,并繪制了動態(tài)再結(jié)晶圖。

    Abstract:

    Flow behavior and dynamic recrystallization (DRX) critical conditions of 25vol.% B4Cp/6061Al composite have been investigated by isothermal compression tests at temperatures ranging from 350℃ to 500℃ with strain rates of 0.001s-1-1s-1. The stress-strain curves show that DRX is the mainly softening mechanism of the composite, and an Arrhenius-type equation is developed used peak stress. Based on the strain hardening rate curves (θ-σ), the critical strains (εc) and critical stress (σc) are identified to express the initiation of DRX. The results show that there is a liner relationship between σc and σp: σc= 0.8374σp- 0.33708. The Zener-Hollomon parameter is also introduced to describe the effect of deformation conditions on critical conditions: εc=2.39×10-4Z0.11022. In addition, the steady-state strains (εss) are determined by the θ-ε curves, and then the DRX diagram is established.

    參考文獻
    相似文獻
    引證文獻
引用本文

劉生璞,李德富,郭勝利. B4Cp/6061Al復(fù)合材料動態(tài)再結(jié)晶臨界條件[J].稀有金屬材料與工程,2017,46(7):1815~1820.[Liu Shengpu, Li Defu, Guo Shengli. Critical Conditions of Dynamic Recrystallization for B4Cp/6061Al composite[J]. Rare Metal Materials and Engineering,2017,46(7):1815~1820.]
DOI：[doi]

復(fù)制
文章指標
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2016-11-15
  • 最后修改日期:2017-01-09
  • 錄用日期:2017-02-20
  • 在線發(fā)布日期: 2017-11-14
  • 出版日期: