2O3)擴散阻擋層和Ni-Cr-Al合金先驅(qū)層,制備得到SiCf/Ni-Cr-Al先驅(qū)絲。研究了涂層的形貌、成分和相組成,以及涂層對SiC纖維力學(xué)性能的影響。對先驅(qū)絲在850℃/150h和900℃/150h進行真空熱處理。研究結(jié)果表明：Al2O3涂層均勻致密,呈非晶態(tài),Ni-Cr-Al合金涂層成分分布均勻,與靶材成分相當(dāng)；涂層與SiC纖維結(jié)合良好,且對SiC纖維力學(xué)性能影響較?。幌闰?qū)絲在真空熱處理后,Ni-Cr-Al合金層仍保持完整,(Al+Al2O3)涂層有效的抑制了界面處元素擴散和化學(xué)反應(yīng),保證了高性能的SiCf/Ni-Cr-Al復(fù)合材料的制備。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
SiC纖維增強Ni-Cr-Al合金復(fù)合材料先驅(qū)絲的制備
DOI:
作者:
作者單位:

中國科學(xué)院金屬研究所,中國科學(xué)院金屬研究所,中國科學(xué)院金屬研究所,中國科學(xué)院金屬研究所,中國科學(xué)院金屬研究所,中國科學(xué)院金屬研究所

作者簡介:

通訊作者:

中圖分類號:

TG146.2

基金項目:

國家自然科學(xué)基金資助(項目號51371170);


Preparaetion of Precursor Fiber for SiC Fiber Reinforced Ni-Cr-Al Alloy Composites
Author:
Affiliation:

Institute of Metal Research,Chinese Academy of Sciences,Institute of Metal Research,Chinese Academy of Sciences,Institute of Metal Research,Chinese Academy of Sciences,Institute of Metal Research,Chinese Academy of Sciences,Institute of Metal Research,Chinese Academy of Sciences,Institute of Metal Research,Chinese Academy of Sciences

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    采用對靶設(shè)計的磁控濺射法在SiC纖維表面先后沉積了(Al+Al2O3)擴散阻擋層和Ni-Cr-Al合金先驅(qū)層,制備得到SiCf/Ni-Cr-Al先驅(qū)絲。研究了涂層的形貌、成分和相組成,以及涂層對SiC纖維力學(xué)性能的影響。對先驅(qū)絲在850℃/150h和900℃/150h進行真空熱處理。研究結(jié)果表明：Al2O3涂層均勻致密,呈非晶態(tài),Ni-Cr-Al合金涂層成分分布均勻,與靶材成分相當(dāng)；涂層與SiC纖維結(jié)合良好,且對SiC纖維力學(xué)性能影響較??；先驅(qū)絲在真空熱處理后,Ni-Cr-Al合金層仍保持完整,(Al+Al2O3)涂層有效的抑制了界面處元素擴散和化學(xué)反應(yīng),保證了高性能的SiCf/Ni-Cr-Al復(fù)合材料的制備。

    Abstract:

    SiCf/Ni-Cr-Al precursor wire has been obtained by deposition of (Al+Al2O3) diffusion barrier layers and Ni-Cr-Al alloy coating on the surface of SiC fiber via magnetron sputtering. The morphology, composition and the phase of coatings were studied, and the influence of the coatings on the mechanical property of SiC fiber was investigated. The precursor wires were treated in vacuum at 850℃ and 900℃ for 150 hours. The results show that (Al+Al2O3) coating is uniform and dense, the Al2O3 coating is in the form of amorphous,and the composition of Ni-Cr-Al alloy coating is close to that of Ni alloy target. The (Al+Al2O3) layer and Ni-Cr-Al layer combine well with SiC fiber and have extremely slight negative effect on the tensile strength. After heat treatment in vacuum, the Ni-Cr-Al alloy coating remains intact, and Al2O3 coating effectively blocks the element diffusion and restricts the reaction between SiC fiber and Ni-Cr-Al alloy, which can ensure the preparation of high performance of SiCf/Ni-Cr-Al composites.

    參考文獻
    相似文獻
    引證文獻
引用本文

牛西茜,汪龍,張浩強,石南林,宮駿,孫超. SiC纖維增強Ni-Cr-Al合金復(fù)合材料先驅(qū)絲的制備[J].稀有金屬材料與工程,2017,46(11):3550~3555.[Niu Xixi, Wang Long, Zhang Haoqiang, Shi Nanlin, Gong Jun, Sun Chao. Preparaetion of Precursor Fiber for SiC Fiber Reinforced Ni-Cr-Al Alloy Composites[J]. Rare Metal Materials and Engineering,2017,46(11):3550~3555.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2016-08-23
  • 最后修改日期:2016-10-15
  • 錄用日期:2016-12-06
  • 在線發(fā)布日期: 2017-12-13
  • 出版日期: