Effect of low temperature solution and aging treatment on Mechanical properties of TC4 Titanium alloy bars
Author:
Affiliation:

wst,,,,,,

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計(jì)
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評(píng)論
    摘要:

    兩相鈦合金中,針對(duì)亞穩(wěn)β相在加工及處理過程中的轉(zhuǎn)變及對(duì)性能的影響研究較為鮮見,本文研究了TC4鈦合金棒材經(jīng)650℃和700℃固溶處理后的組織和性能變化。結(jié)果表明：對(duì)熱加工態(tài)的TC4鈦合金進(jìn)行低于650℃的固溶熱處理,材料的拉伸性能和顯微組織變化不大。 經(jīng)過700℃固溶熱處理,TC4鈦合金棒材強(qiáng)度明顯降低,屈服強(qiáng)度相對(duì)于熱處理前降低77MPa且屈強(qiáng)比明顯低于普通退火。時(shí)效熱處理后,合金的強(qiáng)度顯著提高,400℃時(shí)效后抗拉強(qiáng)度達(dá)到1020MPa,相對(duì)于熱處理前提高53MPa。顯微組織分析結(jié)果表明,熱加工后的TC4棒材顯微組織由初生α相、次生α相以及殘余β相組成。熱處理過程中,殘余β相的轉(zhuǎn)變是影響合金拉伸性能變化的主要原因。

    Abstract:

    Effect of solution and aging heat treatment with lower temperature on the microstructures and mechanical properties of TC4 alloy bars were studied in this paper. Different heat treatment schedules were adopted and compared on titanium bars with fully equiaxed microstructure. The results show that with 700℃ solution temperature, strength of TC4 alloy decreases. Compared with the as forged alloy, rupture strength of the alloy reduce 77 MPa after solution treatment at 700℃. Aging at temperatures lower than 650℃ has great influence on the mechanical of TC4 alloy, aging at 400℃ could get ideal match of strength and plasticity.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

杜剛,孫小平,高玉社,王瑋東,侯峰起,付寶全,劉向宏.低溫固溶及時(shí)效處理對(duì)TC4合金棒材組織及力學(xué)性能的影響[J].稀有金屬材料與工程,2018,47(6):1941~1944.[Du Gang, Sun Xiaoping, Gao yushe, Wang Weidong, Hou Fengqi, Fu Baoquan, Liu Xianghong. Effect of low temperature solution and aging treatment on Mechanical properties of TC4 Titanium alloy bars[J]. Rare Metal Materials and Engineering,2018,47(6):1941~1944.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點(diǎn)擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2016-05-10
  • 最后修改日期:2016-07-30
  • 錄用日期:2016-08-17
  • 在線發(fā)布日期: 2018-09-06
  • 出版日期: