24Y5相組成,沒有發(fā)現(xiàn)含Sm相的生成。隨著溫度從20 oC升高到300 oC,合金的抗拉強度均高于200 MPa,沒有明顯變化。合金強度對溫度不敏感,變化幅度低于10 MPa。其抗拉強度穩(wěn)定性優(yōu)于發(fā)展最為成功的商用耐熱鎂合金WE54,原因可主要歸結(jié)于因Sm固溶而增強的強化相Mg24Y5硬度的穩(wěn)定性。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
時效硬化Mg-10Y-1.5Sm合金的強度穩(wěn)定性
DOI:
作者:
作者單位:

河南科技大學 材料科學與工程學院,河南科技大學 材料科學與工程學院,河南科技大學 材料科學與工程學院

作者簡介:

通訊作者:

中圖分類號:

TG146.2

基金項目:

國家自然科學基金項目（面上項目，重點項目，重大項目）


Strength stability of aging hardened Mg-10Y-1.5Sm alloy
Author:
Affiliation:

School of Materials Science and Engineering,Henan University of Science and Technology,School of Materials Science and Engineering,Henan University of Science and Technology,School of Materials Science and Engineering,Henan University of Science and Technology

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    采用組織分析和拉伸試驗,研究了時效硬化Mg-10Y-1.5Sm(質(zhì)量分數(shù),%)合金抗拉強度的穩(wěn)定性。結(jié)果表明,Mg-10Y-1.5Sm合金的顯微組織由α-Mg基體和Mg24Y5相組成,沒有發(fā)現(xiàn)含Sm相的生成。隨著溫度從20 oC升高到300 oC,合金的抗拉強度均高于200 MPa,沒有明顯變化。合金強度對溫度不敏感,變化幅度低于10 MPa。其抗拉強度穩(wěn)定性優(yōu)于發(fā)展最為成功的商用耐熱鎂合金WE54,原因可主要歸結(jié)于因Sm固溶而增強的強化相Mg24Y5硬度的穩(wěn)定性。

    Abstract:

    The tensile strength stability of aging hardened Mg-10Y-1.5Sm (mass fraction, %) alloy was investigated by microstructure analysis and tensile tests. The results show that the microstructure of Mg-10Y-1.5Sm alloy consists of α-Mg matrix and Mg24Y5 phase and the formation of Sm-containing phase is not observed. With the increase of temperature from 20 oC to 300 oC, the tensile strength exceeds 200 MPa and has no obvious change. It is insensitive to temperature and the variation range is less than 10 MPa. The strength stability is superior to that of heat resistant magnesium alloy WE54 developed most successfully. The reason is mainly attributed to the hardness stability of strengthening phase Mg24Y5 enhanced by dissolved Sm.

    參考文獻
    相似文獻
    引證文獻
引用本文

張 清,陳 君,李全安.時效硬化Mg-10Y-1.5Sm合金的強度穩(wěn)定性[J].稀有金屬材料與工程,2018,47(3):799~802.[Zhang Qing, Chen Jun, Li Quan-an. Strength stability of aging hardened Mg-10Y-1.5Sm alloy[J]. Rare Metal Materials and Engineering,2018,47(3):799~802.]
DOI：[doi]

復制
文章指標
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2016-03-24
  • 最后修改日期:2016-08-24
  • 錄用日期:2016-09-18
  • 在線發(fā)布日期: 2018-04-11
  • 出版日期: