Synthesis and characterization of MnO/C micro-nano composites
Author:
Affiliation:

712th research institute,CSCI Wuhan,College of Environmental and Energy Engineering,Beijing University of Technology,Beijing,College of Environmental and Energy Engineering,Beijing University of Technology,Beijing,College of Environmental and Energy Engineering,Beijing University of Technology,Beijing

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    以醋酸錳、乙二醇、草酸二水化合物為原料,以聚乙烯吡咯烷酮(PVP)、葡萄糖、間苯二酚為碳源,通過沉淀法輔以熱處理,制備出了碳包覆的微納米結(jié)構(gòu)MnO/C復(fù)合材料。利用XRD、SEM、TEM和電化學(xué)測試研究MnO/C復(fù)合材料的結(jié)構(gòu)、形貌和電化學(xué)性能。研究結(jié)果表明,以PVP為碳源通過沉淀法制備的MnO/C材料具有微納米復(fù)合結(jié)構(gòu)且材料表面均勻包覆3 nm左右的碳層。該材料作為鋰電負(fù)極材料在100 mA/g的恒流充放電下循環(huán)50次可逆容量達(dá)到586.1 mAh/g,并且經(jīng)過大電流充放電后仍然表現(xiàn)了優(yōu)異的結(jié)構(gòu)穩(wěn)定性。

    Abstract:

    The carbon-coated MnO/C micro-nano composites were fabricated via precipitation, followed by thermal treatment, with Mn(CHCOO)2?H2O, Ethylene glycol and Oxalic acid dehydrate as the reactants, PVP, C6H12O6 and C6H4(OH)2 as carbon. The structure, Morphology and electrochemical properties of the MnO/C materials were characterized with X-ray diffraction, scanning electro microscope, transmission electro microscope and electrochemical experiments. The results indicate that the MnO/C composite with a 3nm carbon-coated layer may be a good anode material for lithium-ion battery. It shows an excellent cycling stability of 586.1mAh/g after 50 cycles and excellent structural stability after several high-current charge and discharge courses.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

周章華,趙悟睿,趙惠慧,張麗娟.微納米結(jié)構(gòu)MnO/C材料的制備與儲鋰性能研究[J].稀有金屬材料與工程,2018,47(4):1287~1292.[ZHOU zhanghua, ZHAO wurui, ZHAO huihui, ZHANG lijuan. Synthesis and characterization of MnO/C micro-nano composites[J]. Rare Metal Materials and Engineering,2018,47(4):1287~1292.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2016-03-11
  • 最后修改日期:2016-04-14
  • 錄用日期:2016-04-27
  • 在線發(fā)布日期: 2018-05-31
  • 出版日期: