68.4-xCo7.6Si7B10P5C2Crx (x=0, 1, 2, 3)非晶合金,并分別使用單輥急冷甩帶法和銅模鑄造法制備了帶狀和棒狀樣品。借助XRD、DSC、DTA表征該非晶合金系的熱力學(xué)性能與非晶形成能；并進(jìn)一步采用電化學(xué)動(dòng)電位極化曲線法研究了該非晶合金系在硫酸溶液中的的耐腐蝕性能。實(shí)驗(yàn)結(jié)果表明,通過微量添加Cr元素的方法,使該合金系的非晶形成能普遍提高,當(dāng)Cr元素添加量為2%時(shí),獲得了該系列非晶合金中的最大過冷液體區(qū)間(ΔTx=57K),并且成功制備了直徑為5mm的圓棒狀樣品；同時(shí),由于Cr元素的添加,在1N濃度的硫酸溶液中,材料表面上形成富含Cr元素的保護(hù)層,可以有效阻止材料內(nèi)部的進(jìn)一步腐蝕,耐腐蝕性能明顯得到改善。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
Cr元素對Fe基塊體非晶合金形成能及腐蝕性能影響的研究
DOI:
作者:
作者單位:

遼寧科技大學(xué),遼寧科技大學(xué),遼寧科技大學(xué),遼寧科技大學(xué),遼寧科技大學(xué),遼寧科技大學(xué),日本埼玉工業(yè)大學(xué),日本東北大學(xué)金屬材料研究所

作者簡介:

通訊作者:

中圖分類號:

基金項(xiàng)目:

國家自然科學(xué)基金(項(xiàng)目號51501084)；教育部留學(xué)回國人員科研啟動(dòng)基金；遼寧省教育評價(jià)協(xié)會課題(PJHYYB15077)；鞍山市科技計(jì)劃項(xiàng)目；遼寧科技大學(xué)專項(xiàng)基金(2014QN01, 2015RC01,cxcy-2015-11)。


Effect of Cr Element on the Forming Ability and Corrosion Properties of Fe-based Bulk Amorphous Alloys
Author:
Affiliation:

University of Science and Technology Liaoning USTL,University of Science and Technology Liaoning USTL,,,University of Science and Technology Liaoning USTL,,,

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計(jì)
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    利用微合金化技術(shù),制備了Fe68.4-xCo7.6Si7B10P5C2Crx (x=0, 1, 2, 3)非晶合金,并分別使用單輥急冷甩帶法和銅模鑄造法制備了帶狀和棒狀樣品。借助XRD、DSC、DTA表征該非晶合金系的熱力學(xué)性能與非晶形成能；并進(jìn)一步采用電化學(xué)動(dòng)電位極化曲線法研究了該非晶合金系在硫酸溶液中的的耐腐蝕性能。實(shí)驗(yàn)結(jié)果表明,通過微量添加Cr元素的方法,使該合金系的非晶形成能普遍提高,當(dāng)Cr元素添加量為2%時(shí),獲得了該系列非晶合金中的最大過冷液體區(qū)間(ΔTx=57K),并且成功制備了直徑為5mm的圓棒狀樣品；同時(shí),由于Cr元素的添加,在1N濃度的硫酸溶液中,材料表面上形成富含Cr元素的保護(hù)層,可以有效阻止材料內(nèi)部的進(jìn)一步腐蝕,耐腐蝕性能明顯得到改善。

    Abstract:

    Using micro alloy technology, Fe68.4-xCo7.6Si7B10P5C2Crx (x=0, 1, 2, 3) bulk amorphous alloys were prepared. The ribbon and rod samples were prepared by single-roller melt spinning and copper mold casting, respectively. The thermodynamic properties and forming ability of the bulk amorphous alloys were characterized by using XRD, DSC and DTA. Further, the corrosion behaviors of the amorphous alloys were tested in H2SO4 solution by using potentiodynamic polarization method. The experimental results showed that the forming ability of the amorphous alloys increased with the addition of Cr element. Moreover, in the 1N H2SO4 solution, a protective layer rich in Cr elements formed on the surfacr of the alloy because of the addition of Cr element, which can effectively prevent the further corrosion of the material. Therefore, the corrosion resistance was improved significantly

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

熊斌,李雪,鄭繼波,黎曦寧,盧公昊,王振敏,巨東英,牧野彰宏. Cr元素對Fe基塊體非晶合金形成能及腐蝕性能影響的研究[J].稀有金屬材料與工程,2018,47(2):701~704.[Xiong bin, Li Xue, zheng jibo, Li Xining, Lu gonghao, Wang Zhenmin, Ju dongying, Makino Akihiro. Effect of Cr Element on the Forming Ability and Corrosion Properties of Fe-based Bulk Amorphous Alloys[J]. Rare Metal Materials and Engineering,2018,47(2):701~704.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點(diǎn)擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2015-12-08
  • 最后修改日期:2016-04-19
  • 錄用日期:2016-05-18
  • 在線發(fā)布日期: 2018-03-15
  • 出版日期: