熱氧化TC4合金在模擬油田介質(zhì)中的沖蝕磨損行為
DOI:
作者:
作者單位:

太原理工大學(xué),太原理工大學(xué),太原理工大學(xué),太原理工大學(xué),太原理工大學(xué),太原理工大學(xué),太原理工大學(xué),太原理工大學(xué)

作者簡介:

通訊作者:

中圖分類號:

TG115.5 8；TG146.2 3；TG178

基金項目:

國家自然科學(xué)基金(51501125)；中國博士后科學(xué)基金(2012M520604)；山西省青年科技基金(2013021013-2)；陜西省科技新星基金(2013KJXX-08)


Erosive Wear Behavior of Thermal Oxidized TC4 Alloy in Simulated Oilfield Medium
Author:
Affiliation:

Taiyuan University of Technology,Taiyuan,Taiyuan University of Technology,Taiyuan,Taiyuan University of Technology,Taiyuan,Taiyuan University of Technology,Taiyuan,Taiyuan University of Technology,Taiyuan,Taiyuan University of Technology,Taiyuan,Taiyuan University of Technology,Taiyuan,Taiyuan University of Technology,Taiyuan

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    采用熱氧化技術(shù)對TC4合金進行表面處理，使用掃描電鏡，能譜儀，光學(xué)顯微鏡，輝光光譜分析儀和X射線衍射儀分析熱氧化層的特征，研究了熱氧化TC4合金在模擬油田介質(zhì)中的沖蝕磨損行為。結(jié)果表明：熱氧化層主要由金紅石相組成，熱氧化層具有更高的表面硬度，更低的沖蝕磨損失重。熱氧化處理顯著提高了TC4合金在模擬油田介質(zhì)中的抗沖蝕磨損性能。

    Abstract:

    Thermal oxidation (TO) process was applied to treat TC4 alloy. Microstructural characteristics of the TO layer were analyzed using scanning electron microscope (SEM), energy dispersive spectrometer (EDS), optical microscope (OM), glow discharge optical emission spectrometer analysis (GDOES) and X-ray diffraction (XRD). Erosive wear behaviors of the TO treated TC4 alloy in CO2-saturated simulated oilfield medium were investigated. The results showed that the obtained TO layer was mainly composed of rutile TiO2 phase. The TO layer presented higher surface hardness and lower mass loss values. TO treatment had significantly improve the resistance to erosive wear of TC4 alloy.

    參考文獻
    相似文獻
    引證文獻
引用本文

林乃明,鄒嬌娟,田偉,馬永,王振霞,秦林,王志華,唐賓.熱氧化TC4合金在模擬油田介質(zhì)中的沖蝕磨損行為[J].稀有金屬材料與工程,2017,46(12):4000~4005.[Lin Naiming, Zou Jiaojuan, Tian Wei, Ma Yong, Wang Zhenxia, Qin Lin, Wang Zhihua, Tang Bin. Erosive Wear Behavior of Thermal Oxidized TC4 Alloy in Simulated Oilfield Medium[J]. Rare Metal Materials and Engineering,2017,46(12):4000~4005.]
DOI：[doi]

復(fù)制
文章指標
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2015-09-13
  • 最后修改日期:2015-10-06
  • 錄用日期:2015-10-15
  • 在線發(fā)布日期: 2018-01-04
  • 出版日期: