Effect of compounds precipitation on thermal conductivity of Mg-Sn binary alloy
Author:
Affiliation:

Key Laboratory for Anisotropy and Texture of Materials Ministry of Education,Northeastern University,Key Laboratory for Anisotropy and Texture of Materials Ministry of Education,Northeastern University,National Engineering Research Center for Magnesium Alloys,Chongqing University,National Engineering Research Center for Magnesium Alloys,Chongqing University,National Engineering Research Center for Magnesium Alloys,Chongqing University,National Engineering Research Center for Magnesium Alloys,Chongqing University

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    本文研究了添加不同含量的Sn(3 wt.%, 6 wt.%, 9 wt.%)對鑄態(tài)、固溶態(tài)及時效態(tài)Mg-Sn二元合金導(dǎo)熱性能的影響。結(jié)果表明,鑄態(tài)及固溶處理態(tài)Mg-Sn合金的熱導(dǎo)率均隨著Sn元素含量的增加不斷降低,其中含Sn含量最多的固溶態(tài)Mg-10Sn合金所對應(yīng)的熱導(dǎo)率降低至52.6W/m.K；同固溶態(tài)合金相比,相同溶質(zhì)含量的鑄態(tài)合金的熱導(dǎo)率更高。Mg-Sn合金的熱導(dǎo)率隨時效的進行逐漸升高,Mg-3Sn,Mg-6Sn及Mg-10Sn合金的熱導(dǎo)率分別最終可達到125W/m.K、120W/m.K及110W/m.K。分析表明鎂合金熱導(dǎo)率的不斷升高可以歸結(jié)于基體的純化效應(yīng),Sn元素的原子大小、核外電子分布以及化合價等均會對Mg-Sn合金的導(dǎo)熱性能產(chǎn)生影響。

    Abstract:

    In this work, effects of the Sn additions (3 wt.%, 6 wt.%, 9 wt.%)on thermal conductivities of the as-cast, as-homogenized and as-aged Mg-Sn binary alloys were investigated. The results showed that thermal conductivities of the both as-cast and as-homogenized Mg-Sn alloys decreased with content of Sn addition, and corresponding thermal conductivity of the as-homogenized Mg-10Sn decreased as 52.6W/m.K. Compared with as-homogenized sample, thermal conductivity of the as-cast alloy with the same solute content was lower. Thermal conductivity of the Mg-Sn alloy increased with aging treatment, and thermal conductivities of the as-aged Mg-3Sn, Mg-6Sn and Mg-10Sn alloys saturated as 125W/m.K, 120W/m.K and 110W/m.K respectively. Purification of the Mg matrix contributed to the thermal conductivity increment, and atomic size, electron configuration and the charge of the Sn element determined the thermal conductivity of the Mg-Sn alloy.

    參考文獻
    相似文獻
    引證文獻
引用本文

潘虎成,黃韞淼,高正源,黃秋燕,彭 建,潘復(fù)生.化合物相的析出對Mg-Sn二元合金導(dǎo)熱性能的影響[J].稀有金屬材料與工程,2017,46(11):3311~3315.[Hucheng Pan, Yunmiao Huang, Zhengyuan Gao, Qiuyan Huang, Jian Peng, Fusheng Pan. Effect of compounds precipitation on thermal conductivity of Mg-Sn binary alloy[J]. Rare Metal Materials and Engineering,2017,46(11):3311~3315.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2015-09-07
  • 最后修改日期:2015-11-10
  • 錄用日期:2015-12-08
  • 在線發(fā)布日期: 2017-12-13
  • 出版日期: