Microstructure and properties of 2195/2219 dissimilar FSW
Author:
Affiliation:

School of Material Science and Engineering, Shanghai Jiao Tong University,,,,,,,

Fund Project:

Scientific Research Fund of Heilongjiang Provincial Education Department (11531319)

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問(wèn)統(tǒng)計(jì)
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評(píng)論
    摘要:

    本研究對(duì)2195-T8與2219-T6薄板進(jìn)行了攪拌摩擦焊接實(shí)驗(yàn)。在恒定轉(zhuǎn)速(TRS)的條件下,研究了接頭性能與焊接走速(TS)和不同前進(jìn)側(cè)材料之間的關(guān)系。實(shí)驗(yàn)結(jié)果表明在研究采用的參數(shù)范圍內(nèi)提高焊接走速有助于增強(qiáng)接頭的力學(xué)性能；將2195置于前進(jìn)側(cè)的接頭性能要優(yōu)于2219作為前進(jìn)側(cè),而無(wú)論何種材料為前進(jìn)側(cè),斷裂始終發(fā)生在2219一側(cè)的焊核邊界；縱向拉伸的結(jié)果顯示,焊核的力學(xué)性能強(qiáng)于2219一側(cè)焊核邊界材料。同時(shí)本文結(jié)合焊縫組織演化,對(duì)接頭力學(xué)性能的演化規(guī)律做出了分析。

    Abstract:

    2195-T8 and 2219-T6 sheets were successfully welded in the current research.With constant tool rotation speed (TRS), effects of travelling speed (TS) and advancing side material (AS material) on the mechanical properties of the joint were studied. The results indicate that higher travelling speed improves the mechanical properties of the FSW joint. Whichever the AS material was, fracture always occurred at the boundary of the welding nugget zone (WNZ)/thermomechanical affected zone (TMAZ) to the 2219 side. Longitudinal tensile tests show that mechanical property of the WNZ is better than that at the boundary of WNZ/TMAZ to the 2219 size.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

房湛,王凡,尹玉環(huán),董豐波,徐琛,張聃,陳科,單愛(ài)黨.2195/2219異種材料攪拌摩擦焊接頭的組織與性能[J].稀有金屬材料與工程,2017,46(7):2017~2021.[Fang Zhan, Wang Fan, Yin Yuhuan, Dong Fengbo, Xu Chen, Zhang Dan, Chen Ke, Shan Aidang. Microstructure and properties of 2195/2219 dissimilar FSW[J]. Rare Metal Materials and Engineering,2017,46(7):2017~2021.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點(diǎn)擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2015-03-25
  • 最后修改日期:2015-12-24
  • 錄用日期:2016-01-14
  • 在線發(fā)布日期: 2017-11-14
  • 出版日期: