Isothermal Section of Zr-Cr-Cu Ternary System at 700℃
Author:
Affiliation:

Guangxi University,Guangxi University,State Nuclear Bao Ti Zirconium Industry Company,Guangxi University for Nationalities,Guangxi University for Nationalities,Guangxi University for Nationalities

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問(wèn)統(tǒng)計(jì)
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評(píng)論
    摘要:

    利用X射線粉末衍射法（XRD），掃描電子顯微鏡（SEM）和能譜分析（EDX）等方法首次測(cè)定了Zr-Cr-Cu三元系700℃等溫截面。研究結(jié)果表明，此截面由10個(gè)單相區(qū)、18個(gè)兩相區(qū)和9個(gè)三相區(qū)組成。第三組元Cr的加入，導(dǎo)致高溫CuZr相共析分解溫度下降，在700℃時(shí)形成穩(wěn)定的三元相τ。研究確定體系中富鋯角和富銅角不存在三元化合物。富鋯區(qū)合金由ZrCr2、(α-Zr)和 CuZr2三相構(gòu)成。富銅區(qū)合金由(Cr)、(Cu)和Cu5Zr相構(gòu)成。

    Abstract:

    The isothermal section of the Zr-Cr-Cu ternary system at 700 ℃ was investigated by using X-ray diffraction, scanning electron microscope and energy dispersive analysis. It was composed of 10 single-phase regions, 18 two-phase regions and 9 three-phase regions. The τ phase was observed to occur as a stable ternary phase at 700 ℃ when Cr was introduced. No ternary compound was observed in the Zr-rich corner and Cu-rich corner. The alloys in Zr-rich corner was consists of ZrCr2, (α-Zr) and CuZr2, while those in the Cu-rich corner was consists of (Cr), (Cu) and Cu5Zr.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

張敏,歐陽(yáng)義芳,袁改煥,唐軼媛,祝金明,梁建烈. Zr-Cr-Cu三元系700℃等溫截面[J].稀有金屬材料與工程,2016,45(5):1240~1244.[zhang min, ouyang yifang, yuan gaihuan, tang yiyuan, zhu jinming, liang jianlie. Isothermal Section of Zr-Cr-Cu Ternary System at 700℃[J]. Rare Metal Materials and Engineering,2016,45(5):1240~1244.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點(diǎn)擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2014-05-14
  • 最后修改日期:2014-06-30
  • 錄用日期:2014-07-28
  • 在線發(fā)布日期: 2016-06-02
  • 出版日期: