Effect of Niobium on the Microstructure and Wear Resistance of Nickel-Based Alloy Coating by Laser Cladding
DOI:
作者:
作者單位:

作者簡介:

通訊作者:

中圖分類號:

基金項目:

National Natural Science Foundation of China (50675136, 50375096)


Effect of Niobium on the Microstructure and Wear Resistance of Nickel-Based Alloy Coating by Laser Cladding
Author:
Affiliation:

Fund Project:

National Natural Science Foundation of China (50675136, 50375096)

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    The nickel-based alloys with different Nb contents were deposited on AISI 1045 carbon steel by laser cladding. The effect of Nb on the microstructures of the nickel-based alloy coatings was investigated using scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques. The result show that the microstructures of the Nb-modified nickel-based alloy coatings are mainly composed of γ-Ni dendrites, interdendritic eutectics, CrB type chromium borides, and dispersed NbC particles. It is found that the addition of Nb will lead to the precipitation of the NbC particles and M23C6 type carbides instead of the M7C3, and M23C6 type carbides can be observed in the Nb-free nickel-based alloy coating. The microhardness and wear resistance of the coatings increase with the increase of Nb contents. The improvement of the wear resistance of the Nb-modified nickel-based alloy coatings is attributed to the microstructural change and phase variation.

    Abstract:

    The nickel-based alloys with different Nb contents were deposited on AISI 1045 carbon steel by laser cladding. The effect of Nb on the microstructures of the nickel-based alloy coatings was investigated using scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques. The result show that the microstructures of the Nb-modified nickel-based alloy coatings are mainly composed of γ-Ni dendrites, interdendritic eutectics, CrB type chromium borides, and dispersed NbC particles. It is found that the addition of Nb will lead to the precipitation of the NbC particles and M23C6 type carbides instead of the M7C3, and M23C6 type carbides can be observed in the Nb-free nickel-based alloy coating. The microhardness and wear resistance of the coatings increase with the increase of Nb contents. The improvement of the wear resistance of the Nb-modified nickel-based alloy coatings is attributed to the microstructural change and phase variation.

    參考文獻
    相似文獻
    引證文獻
引用本文

Dong Gang, Yan Biao, Deng Qilin, Yu Ting. Effect of Niobium on the Microstructure and Wear Resistance of Nickel-Based Alloy Coating by Laser Cladding[J].稀有金屬材料與工程,2011,40(6):973~977.[Dong Gang, Yan Biao, Deng Qilin, Yu Ting. Effect of Niobium on the Microstructure and Wear Resistance of Nickel-Based Alloy Coating by Laser Cladding[J]. Rare Metal Materials and Engineering,2011,40(6):973~977.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2010-06-20
  • 最后修改日期:
  • 錄用日期:
  • 在線發(fā)布日期:
  • 出版日期: