最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
Preparation and Performance of Ceria Doped Two-Component deNOx Monolithic Catalysts at Low Temperature
DOI:
作者:
作者單位:

作者簡介:

通訊作者:

中圖分類號:

基金項目:

National Natural Science Foundation of China (50872052); PhD Student Innovation Foundation of Jiangsu Province


Preparation and Performance of Ceria Doped Two-Component deNOx Monolithic Catalysts at Low Temperature
Author:
Affiliation:

Fund Project:

National Natural Science Foundation of China (50872052); PhD Student Innovation Foundation of Jiangsu Province

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    Abstract: The (V-W-Ti-O)x (Cu-Al-O)1-x (Ce-O)0.03, (x=0.9, 0.8) deNOx monolithic catalysts were prepared by low temperature co-sintering (LTC) within the sintering temperature range of 650-850 °C. The effects of sintering temperature on the mechanical strength, porosity and water absorption of the monolithic catalysts and the effect of reaction temperature on catalytic activity were investigated. The microscopic structure of the catalysts was analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and fourier infrared spectroscopic analysis (FT-IR). Results show that catalysts are porous in micro-structure and grains are distributed uniformly. The crystallographic forms are mainly TiO2 (rutile), TiVO4, WV2O6, CeVO4, Cu2V2O7, AlV2O4, CuAlMnO4 and Cu1.9V12O29. For the reforming monolithic catalysts sintered at 700 °C for 2 h, the two-component catalysts exhibit high catalytic activities in the low temperature range of 100-200 °C and their bending strength reaches to 45.5 MPa. The NO conversion of (V-W-Ti-O)0.8 (Cu-Al-O)0.2 (Ce-O)0.03 monolithic catalyst corresponds to 75.9% at reactor temperature of 150 °C.

    Abstract:

    Abstract: The (V-W-Ti-O)x (Cu-Al-O)1-x (Ce-O)0.03, (x=0.9, 0.8) deNOx monolithic catalysts were prepared by low temperature co-sintering (LTC) within the sintering temperature range of 650-850 °C. The effects of sintering temperature on the mechanical strength, porosity and water absorption of the monolithic catalysts and the effect of reaction temperature on catalytic activity were investigated. The microscopic structure of the catalysts was analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and fourier infrared spectroscopic analysis (FT-IR). Results show that catalysts are porous in micro-structure and grains are distributed uniformly. The crystallographic forms are mainly TiO2 (rutile), TiVO4, WV2O6, CeVO4, Cu2V2O7, AlV2O4, CuAlMnO4 and Cu1.9V12O29. For the reforming monolithic catalysts sintered at 700 °C for 2 h, the two-component catalysts exhibit high catalytic activities in the low temperature range of 100-200 °C and their bending strength reaches to 45.5 MPa. The NO conversion of (V-W-Ti-O)0.8 (Cu-Al-O)0.2 (Ce-O)0.03 monolithic catalyst corresponds to 75.9% at reactor temperature of 150 °C.

    參考文獻
    相似文獻
    引證文獻
引用本文

Shen Yuesong, Yu Yong, Qiu Tai, Zhu Shemin. Preparation and Performance of Ceria Doped Two-Component deNOx Monolithic Catalysts at Low Temperature[J].稀有金屬材料與工程,2011,40(6):967~972.[Shen Yuesong, Yu Yong, Qiu Tai, Zhu Shemin. Preparation and Performance of Ceria Doped Two-Component deNOx Monolithic Catalysts at Low Temperature[J]. Rare Metal Materials and Engineering,2011,40(6):967~972.]
DOI：[doi]

復(fù)制
文章指標
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2010-06-20
  • 最后修改日期:
  • 錄用日期:
  • 在線發(fā)布日期:
  • 出版日期: