最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

+高級檢索
Microstructure and Properties of Friction Stir Welded Joints of Al-Mg-Sc Alloy Plates
DOI:
作者:
作者單位:

作者簡介:

通訊作者:

中圖分類號:

基金項(xiàng)目:

Postdoctoral Science Foundation of Central South University


Microstructure and Properties of Friction Stir Welded Joints of Al-Mg-Sc Alloy Plates
Author:
Affiliation:

Fund Project:

Postdoctoral Science Foundation of Central South University

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計(jì)
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    The hot rolled and cold rolled-annealed plates of Al-Mg-Sc alloys were welded by friction stir welding. The hardness distribution and the tensile properties of welded joints were measured; the relationships between the microstructure and the properties of the welded joints were studied by means of optical microscopy and transmission electron microscopy. The results show that the welding coefficients of two plates are as high as 92%, the hardness and strength of their weld nugget zones are the lowest, and the fracture of their welded joints happens at weld nugget zones during tensile testing. The decrease of the substructure strengthening caused by the partial recrystallization and the loss of precipitation strengthening from Al3(Sc,Zr) particles result in the decline of hardness and strength of Al-Mg-Sc alloy welded joints.

    Abstract:

    The hot rolled and cold rolled-annealed plates of Al-Mg-Sc alloys were welded by friction stir welding. The hardness distribution and the tensile properties of welded joints were measured; the relationships between the microstructure and the properties of the welded joints were studied by means of optical microscopy and transmission electron microscopy. The results show that the welding coefficients of two plates are as high as 92%, the hardness and strength of their weld nugget zones are the lowest, and the fracture of their welded joints happens at weld nugget zones during tensile testing. The decrease of the substructure strengthening caused by the partial recrystallization and the loss of precipitation strengthening from Al3(Sc,Zr) particles result in the decline of hardness and strength of Al-Mg-Sc alloy welded joints.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

Peng Yongyi, Yin Zhimin, Lei Xuefeng, Pan Qinglin, He Zhenbo. Microstructure and Properties of Friction Stir Welded Joints of Al-Mg-Sc Alloy Plates[J].稀有金屬材料與工程,2011,40(2):201~205.[Peng Yongyi, Yin Zhimin, Lei Xuefeng, Pan Qinglin, He Zhenbo. Microstructure and Properties of Friction Stir Welded Joints of Al-Mg-Sc Alloy Plates[J]. Rare Metal Materials and Engineering,2011,40(2):201~205.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點(diǎn)擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2010-03-05
  • 最后修改日期:
  • 錄用日期:
  • 在線發(fā)布日期:
  • 出版日期: