Ni—Ti焊料部分液相瞬間連接高純Al2O3—Kovar工藝的研究
DOI:
作者:
作者單位:

作者簡介:

通訊作者:

中圖分類號:

TG454

基金項目:


Partial Transient Liquid Phase Bonding of Al_2O_3 to Kovar with a Ni-Ti Filler
Author:
Affiliation:

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計
    • |
  • 參考文獻
    • |
  • 相似文獻
    • |
  • 引證文獻
    • |
  • 資源附件
    • |
  • 文章評論
    摘要:

    通過Ti-Ti活性焊粒部分液相瞬間連接工藝，實現(xiàn)了高純Al2O3陶瓷和可伐合金（Kovar）的氣密性連接。結果表明焊縫區(qū)呈現(xiàn)明顯的“三明治”夾層結構，兩側主要為Ti2Ni金屬間化合物層，中間為較厚的Ti固溶體層。接頭強度最初隨保溫時間延長增加，但與焊接溫度之間沒有明顯的單調關系。

    Abstract:

    An airtight joint between high purity Al2O3 and the alloy Kovar was obtained using a partial transient liquid phase(PTLP) bonding technique with Ni Ti filler.A sandwich structure was observed in the soldered joint two side faces of the sandwich were Ti2Ni and at the center was thick layer of Ti solid solution.Shear testing indicated that the joint strength increased with increase of holding time,although a relationship between strength and joining temperature was not observed.

    參考文獻
    相似文獻
    引證文獻
引用本文

張春光 喬冠軍 等. Ni—Ti焊料部分液相瞬間連接高純Al2O3—Kovar工藝的研究[J].稀有金屬材料與工程,2002,(4):299~302.[Zhang Chunguang, Qiao Guanjun, Jin Zhihao. Partial Transient Liquid Phase Bonding of Al_2O_3 to Kovar with a Ni-Ti Filler[J]. Rare Metal Materials and Engineering,2002,(4):299~302.]
DOI：[doi]

復制
文章指標
  • 點擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:
  • 最后修改日期:2001-04-02
  • 錄用日期:
  • 在線發(fā)布日期:
  • 出版日期: