Study of Titanium Electroplating in Molten NaCl-KCl
Author:
Affiliation:

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問(wèn)統(tǒng)計(jì)
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評(píng)論
    摘要:

    研究了在NaCl-KCl熔融鹽體系中進(jìn)行難熔金屬鈦的電鍍過(guò)程中，K2TiF6添加劑的加入量等因素對(duì)電鍍結(jié)構(gòu)的影響，并對(duì)直流電鍍、脈沖電流電鍍?cè)谌廴邴}電鍍中的應(yīng)用進(jìn)行了比較。使用換向脈沖電流電鍍的新工藝，在碳鋼表面獲得了較好的金屬鈦鍍層。

    Abstract:

    The effect of current density on electroplating titanium in molten NaCl KCl was studied, and a comparison made of the different between the effects of direct current and pulse current in molten salt electroplating. The new technique of pulse current molten salt electroplating and its improvement of e the diffusion limited process was studied. A good Ti coating has been obtained on the surface of metal substrate.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

陳書(shū)榮 謝剛 等. NaCl—KCl熔融體系電鍍鈦的研究[J].稀有金屬材料與工程,2001,(6):471~474.[Chen Shurong, Xie Gang, Zhang Xiongfei, Cui Heng, Wang Dajian . Study of Titanium Electroplating in Molten NaCl-KCl[J]. Rare Metal Materials and Engineering,2001,(6):471~474.]
DOI：[doi]

復(fù)制
文章指標(biāo)
  • 點(diǎn)擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:
  • 最后修改日期:2000-10-14
  • 錄用日期:
  • 在線發(fā)布日期:
  • 出版日期: