oC熱軋,通過分析微觀組織及宏觀織構(gòu)研究了Ti-55531近β合金軋板塑性及極限抗拉強(qiáng)度的各向異性。結(jié)果表明,Ti-55531合金軋板內(nèi)的α相垂直于受力方向分布,并且存在明顯的α相織構(gòu)。α相形貌的取向性使得沿軋向(RD)拉伸時(shí)的裂紋擴(kuò)展阻力大于沿橫向(TD)拉伸,從而具有更好的塑性。宏觀織構(gòu)造成沿RD和TD拉伸滑移系和孿晶的啟動(dòng)存在明顯的差異,從而導(dǎo)致沿TD方向拉伸時(shí)具有更高的極限抗拉強(qiáng)度。"/>

最新色国产精品精品视频,中文字幕日韩一区二区不卡,亚洲有码转帖,夜夜躁日日躁狠狠久久av,中国凸偷窥xxxx自由视频

Ti-55531近β合金軋板拉伸性能各向異性研究
DOI:
作者:
作者單位:

1.湖南金天鈦業(yè)科技有限公司;2.中南大學(xué) 粉末冶金國(guó)家重點(diǎn)實(shí)驗(yàn)室

作者簡(jiǎn)介:

通訊作者:

中圖分類號(hào):

TG301

基金項(xiàng)目:

國(guó)家自然科學(xué)基金(51871242)；湖南省科技創(chuàng)新計(jì)劃項(xiàng)目(2017GK2292)


Research on the anisotropy of tensile properties of Ti-55531 near β alloy rolled plate
Author:
Affiliation:

1.Hunan Goldsky Titanium Industry Technology Co Ltd;2.State Key Laboratory of Powder Metallurgy,Central South University

Fund Project:

  • 摘要
    • |
  • 圖/表
    • |
  • 訪問統(tǒng)計(jì)
    • |
  • 參考文獻(xiàn)
    • |
  • 相似文獻(xiàn)
    • |
  • 引證文獻(xiàn)
    • |
  • 資源附件
    • |
  • 文章評(píng)論
    摘要:

    Ti-55531針片狀α組織在750oC熱軋,通過分析微觀組織及宏觀織構(gòu)研究了Ti-55531近β合金軋板塑性及極限抗拉強(qiáng)度的各向異性。結(jié)果表明,Ti-55531合金軋板內(nèi)的α相垂直于受力方向分布,并且存在明顯的α相織構(gòu)。α相形貌的取向性使得沿軋向(RD)拉伸時(shí)的裂紋擴(kuò)展阻力大于沿橫向(TD)拉伸,從而具有更好的塑性。宏觀織構(gòu)造成沿RD和TD拉伸滑移系和孿晶的啟動(dòng)存在明顯的差異,從而導(dǎo)致沿TD方向拉伸時(shí)具有更高的極限抗拉強(qiáng)度。

    Abstract:

    Ti-55531 alloy with the acicular α initial microstructure was hot rolled at 750oC. The anisotropy of ductility and ultimate tensile properties of Ti-55531 near β alloy rolled plate were studied by analyzing microstructures and macrotextures. The results show that the acicular α phases in the Ti-55531 alloy rolled plate are perpendicular to the direction of the force, and significant α macrotextures are appears. Due to the specific orientation of α phase morphology, the crack propagation resistance along rolling direction (RD) is higher than that along transverse direction (TD), which resulting in better ductility in RD. Macrotextures lead to obvious differences in the action of slip systems and twins along RD and TD, which results in higher ultimate tensile strength along TD.

    參考文獻(xiàn)
    相似文獻(xiàn)
    引證文獻(xiàn)
引用本文

李超,呂亞平,李少君,張曉泳,周科朝. Ti-55531近β合金軋板拉伸性能各向異性研究[J].鈦工業(yè)進(jìn)展,2019,36(4).

復(fù)制
分享
文章指標(biāo)
  • 點(diǎn)擊次數(shù):
  • 下載次數(shù):
  • HTML閱讀次數(shù):
  • 引用次數(shù):
歷史
  • 收稿日期:2019-02-18
  • 最后修改日期:2019-04-01
  • 錄用日期:2019-04-01
  • 在線發(fā)布日期: 2020-10-22
  • 出版日期: